The film formation process in waterborne (WB) epoxy coatings is studied using electrochemical impedance spectroscopy (EIS) measurements and dynamic mechanical analysis (DMA). Ten epoxy coatings with different pigment volume concentration were prepared on standard steel substrates and carefully monitored over four weeks (30 days). It is shown that impedance spectroscopy can serve as a very sensitive tool for accurate experimental detection of the critical pigment volume concentration. We also show that the optimal film formation process and corrosion stability of coatings are greatly affected by the coating pigment volume concentration (PVC) value. As a whole, the study confirms that the optimization of coating protection ability needs to take into account both maximization of the barrier effect as well as maximization of the degree of epoxy-amino cross-linking.

In recent years, many efforts are being devoted to the development of new materials that originate from renewable resources. Polyesters are one of the most important classes of such materials and several bio-based monomers are available for their synthesis. In this work, the development of fully bio-based and solvent-free polyester polyol used for two-component polyurethane coatings on industrial scale is presented. Fossil-based raw materials were substituted with bio-based alternatives that are commercially available on a large scale. Properties of polyols and coatings were determined and measured. Polyols were characterized by the determination of acid number, hydroxyl number, glass transition temperature and refractive index, and measurement of viscosity, color and molecular weight. Coatings were characterized by the determination of mechanical properties, such as hardness, elasticity and impact resistance, and the measurement of optical properties such as gloss, haze, distinctness of image (DOI) and reflected image quality (RIQ) and weathering resistance. Three variations of bio-based polyol were synthesized, then the most suitable version was validated in a clear coat. The results showed that the properties of the bio-based polyol and coating met the requirements and were comparable to the properties of the synthetic counterpart. Results indicate that this newly developed 100% bio-based and solvent-free polyol can be used as a drop-in replacement for synthetic polyol. Furthermore, this work implies that the supply chain is established which allows the green transition in the paint industry.

In this work, the development of FDCA-based polyester resins for coil coatings in industrial environment is presented. The goal of our research was to prepare industrial coatings made from renewable materials with the same performance as the standard coating. Resins with 1%–41% of FDCA on polymer were synthesized and then used in a formulation for primer. Resins were characterized by the determination of non-volatile matter, acid value, hydroxyl value, glass transition temperature, and measurement of viscosity, color and molecular weight. Coatings were characterized by the determination of viscosity, density, non-volatile matter, adhesion, T-test, MEK test, reverse impact, and pencil hardness, as well as the measurement of gloss. FTIR measurements confirmed successful incorporation of FDCA into the polymer. The results showed that resins with up to 31% of FDCA on polymer can be used to prepare coil coating where the properties of resins comply with the requirements and are comparable to the properties of standard resin. Resins had non-volatile matter between 59.0 and 60.1%, an acid value up to 4.6 mg KOH/g, a hydroxyl value of 22.0–24.9 mg KOH/g and viscosity at 23 °C between 6100 and 7500 mPa.s. Nevertheless, with the increase in FDCA in the formulation, discoloration of the resin occurred and incompatibility with the solvents was observed, while up to 10 °C lower glass transition temperatures and up to 28% lower molecular weights of the resins were determined. For coatings prepared from FDCA-based resins, the properties improved or were comparable to the properties of coating prepared from standard resin. Adhesion improved with higher content of FDCA in the resin from 2 Gt to 0 Gt, while all coatings had gloss at 60° of 39%–41%, a reverse impact of 10 J and a pencil hardness of H/2H. T-bend test results varied between 2 T and 0.5 T and the results of the MEK test showed resistance > 100 DR.