In this study, laser-directed energy deposition was applied to build a Ti-rich ternary Ti–Ni–Cu shape-memory alloy onto a TiNi shape-memory alloy substrate to realize the joining of the multifunctional bi-metallic shape-memory alloy structure. The cost-effective Ti, Ni, and Cu elemental powder blend was used for raw materials. Various material characterization approaches were applied to reveal different material properties in two sections. The as-fabricated Ti–Ni–Cu alloy microstructure has the TiNi phase as the matrix with Ti₂Ni secondary precipitates. The hardness shows no high values indicating that the major phase is not hard intermetallics. A bonding strength of 569.1 MPa was obtained by tensile testing, and digital image correlation reveals the different tensile responses of the two sections. Differential scanning calorimetry was used to measure the phase-transformation temperatures. The austenite finishing temperature of higher than 80 °C was measured for the Ti–Ni–Cu alloy section. For the TiNi substrate, the austenite finishing temperature was tested to be near 47 °C at the bottom and around 22 °C at the upper substrate region, which is due to the repeated laser scanning that acts as annealing on the substrate. Finally, the multiple shape-memory effect of two shape-memory alloy sides was tested and identified.

Coaxial wire-based laser metal deposition is a versatile and efficient additive process that can achieve a high deposition rate in the manufacturing of complex structures. In this paper, a three-beam coaxial wire system is studied, with particular attention to the effects of deposition height and laser defocusing on the resulting bead geometry. As the deposition standoff distance changes, so does the workpiece illumination proportion, which describes the ratio of energy going directly into the feedstock wire and into the substrate. Single titanium beads are deposited at varying defocus levels and deposition rates and the bead aspect ratio is measured and analyzed. Over the experimental settings, the defocusing level and deposition rate were found to have a significant effect on the resulting bead aspect ratio. As the defocusing level is increased away from the beam convergence plane, the spot size increases and the deposited track is wider and flatter. Process parameters can be used to tune the deposited material to a desired aspect ratio. In coaxial wire deposition, defocusing provides an adjustment mechanism to the distribution of heat between the wire and substrate and has an important impact on the resulting deposit.

Wire-based additive manufacturing (AM) is at the forefront of complex metal fabrication because of its scalability for large components, potential for high deposition rates, and ease of use. A common goal of wire directed energy deposition (DED) is preserving a stable process throughout deposition. If too little energy is put into the deposition, the wire will stub into the substrate and begin oscillating, creating turbulence within the meltpool. If too much energy exists, the wire will overheat, causing surface tension to take over and create liquid drips as opposed to a solid bead. This paper proposes a computer vision technique to work as both a state detection and event detection system for wire stability. The model utilizes intensity variations along with frame-to-frame difference calculations to determine process stability. Because the proposed model does not rely on machine learning techniques, it is possible for an individual to interpret and adjust as they see fit. The first part of this paper describes creation and implementation of the model. The model’s capability was then evaluated using a 1D laser power experiment, which generated a wide range of stability states across varying powers. The model’s accuracy was evaluated through 3D geometry data gathered from the experimentally deposited beads. The model proved to be both capable and accurate and has potential to be used as a real-time control system with future work.

Coaxial wire-based laser metal deposition is a versatile and efficient additive process that can achieve a high deposition rate in the manufacturing of complex structures. In this paper, a three-beam coaxial wire system is studied, with particular attention given to the effects of the deposition direction and laser beam orientation on the resulting bead geometry symmetry. With the three-beam laser delivery, the laser spot pattern is not always symmetric with respect to the deposition direction. Single titanium beads are deposited in different directions and at varying deposition rates, and the bead profile is quantitatively scored for multiple symmetry measures. Through an analysis of variance, the deposition direction and deposition rate were found to be insignificant with respect to the resulting bead symmetry for the developed measures. The bead symmetry and geometry are important factors in determining if a build is free of critical defects, and in this study, it is shown that the three-beam coaxial wire deposition setup is a directionally independent process.

Wire-based laser metal deposition is an additive manufacturing process that can be used in the efficient manufacturing of complex structures. This paper utilizes a three-beam coaxial laser wire system to explore the effect of process parameters on the resultant deposition density. The reduction in or elimination of defects is important to the mechanical properties of the additively manufactured material and the widespread adoption of additive manufacturing processes. In this work, two-bead-wide walls were deposited under varying experimental conditions, including the traverse feed rate and workpiece illumination proportion. A method for calculating the bead pitch and layer height increment based on the geometry of the deposited material was developed. The deposited samples were micro-CT-scanned to characterize internal defects at a high resolution. The volume of the detected defects was measured and compared to the total sample volume to calculate a defect rate for each run of the experiment. The traverse feed rate and defocusing level were found to have a significant impact on the output defect rate. As these process parameters were increased, the defect rate decreased. Across the experimental levels, the defect volume percentage was reduced from 1.021% to 0.062%. This reduction in internal defect size enhances the material’s mechanical performance and ensures its suitability for aerospace applications.