Climate change and the growing demand for energy have prompted research on alternative eco-friendly energy sources. This study focused on the potential for biogas production from water hyacinth and banana peel waste through physicochemical characterization and batch anaerobic digestion tests. The water hyacinth and banana peel samples were dried, ground, and subjected to elemental, proximate, and fiber content analyses. Subsequently, banana peel waste, water hyacinth stems, and leaves were used for batch anaerobic digestion tests in 500 mL glass flask bottles for 21 days under mesophilic conditions in n = 3 trials. Kruskal–Wallis and Dunnett’s tests were performed to identify the significance of the differences in biogas yield among the samples. The analyses of the elemental, proximate, and fiber contents of water hyacinth and banana peels revealed that they possess a suitable chemical composition and essential nutrients for the production of high-yield biogas. The biogas yields from water hyacinth leaves, stems, and banana peels were 280.15, 324.79, and 334.82 mL/g VS, respectively. These findings indicate that water hyacinth and banana peel waste have significant potential for biogas production.

Carbonization is a thermochemical process that generates thermal energy and charcoal. The system allowing to recover the heat energy for co-, tri- and multi-generation is currently more investigated. The use of multi-generation systems is beneficial from the standpoint of increasing the usage of biomass, energy efficiency and reducing the impact on forests. The aim of this article was to design a carbonizer fit out with a thermal insulation layer and use it for the carbonization of some local biomasses, namely wood chips and teak wood. A heat recovery system was then incorporated into the carbonizer to cogenerate hot water from the thermal energy induced by the carbonization process. The results obtained with the designed carbonizer were 20% and 26% in mass yield respectively for teck wood and wood chips. The system developed that heat recovery was able to generate 25 L/h hot water at 45°C and 50°C during the first and the last phases respectively for wood chips and teak wood carbonization. The introduction of the preheating system induced a significant rise of the water’s temperature. The highest maximum value of the hot water temperature was 62°C obtained during the carbonization of both studied fuels.

In a plant microbial fuel cell (P-MFC), the plant provides the fuel in the form of exudates secreted by the roots, which are oxidised by electroactive bacteria. The immature plant is hampered by low energy yields. Several factors may explain this situation, including the low open-circuit voltage of the plant cell. This is a function of the development of the biofilm formed by the electroactive bacteria on the surface of the anode, in relation to the availability of the exudates produced by the roots. In order to exploit the fertilising role of biochars, a plant cell was developed from C. citratus and grown in a medium to which 5% by mass of coconut shell biochar had been added. Its effect was studied as well as the distance between the electrodes. The potential of Cymbopogon citratus was also evaluated. Three samples without biochar, with inter-electrode distances of 2, 5 and 7 cm, respectively, identified as SCS2, SCS5 and SCS7, and three with the addition of 5 % biochar, with the same inter-electrode distance values, identified as S2, S5 and S7, were prepared. Open-circuit voltage (OCV) measurements were taken at 6 a.m., 1 p.m. and 8 p.m. The results showed that all the samples had high open-circuit voltage values at 1 p.m. Samples containing 5% biochar had open-circuit voltages increased by 16 %, 8.94% and 5.78%, respectively, for inter-electrode distances of 2, 5 and 7 cm compared with those containing no biochar. Furthermore, the highest open-circuit voltage values were obtained for all samples with C. citratus at an inter-electrode distance of 5 cm. The maximum power output of the PMFC with C. citratus in this study was 75.8 mW/m², which is much higher than the power output of PMFCs in recent studies.

Carbon-based electrodes have recently been most widely used in P-MFC due to their desirable properties such as biocompatibility, chemical stability, affordable price, corrosion resistance, and ease of regeneration. In general, carbon-based electrodes, particularly graphite, are produced using a complex process based on petroleum derivatives at very high temperatures. This study aims to produce electrodes from bio-pitch and charcoal powder as an alternative to graphite electrodes. The carbons used to manufacture the electrodes were obtained by the carbonisation of Robinia pseudoacacia and Azadirachta indica wood. These carbons were pulverised, sieved to 50 µm, and used as the raw materials for electrode manufacturing. The binder used was bio-pitch derived from coconut shells as the raw materials. The density and coking value of the bio-pitch revealed its potential as a good alternative to coal-tar pitch for electrode manufacturing. The electrodes were made by mixing 66.50% of each carbon powder and 33.50% of bio-pitch. The resulting mixture was moulded into a cylindrical tube 8 mm in diameter and 80 mm in length. The raw electrodes obtained were subjected to heat treatment at 800 °C or 1000 °C in an inert medium. The electrical resistivity obtained by the four-point method showed that N1000 has an electrical resistivity at least five times lower than all the electrodes developed and two times higher than that of G. Fourier-transform infrared spectroscopy (FTIR) was used to determine the compositional features of the samples and their surface roughness was characterised by atomic force microscopy (AFM). Charge transfer was determined by electrical impedance spectroscopy (EIS). The FTIR of the electrodes showed that N1000 has a spectrum that is more similar to that of G compared to the others. The EIS showed the high ionic mobility of the ions and therefore that N1000 has a higher charge transfer compared to G and the others. AFM analysis revealed that N1000 had the highest surface roughness in this study.