Sludge from cardboard mill is most commonly landfilled, but it could also be recycled on-site into production or reused in some other way. In this study the use of sludge from cardboard mill as stabilizing agent in the stabilization treatment of cadmium polluted sediment was examined. The effectiveness of treatment and long-term leaching behavior of cadmium was evaluated by determining the cumulative percentage of cadmium leached, diffusion coefficients (De) and by applying different leaching tests (semi-dynamic test, toxicity characteristic leaching procedure, waste extraction test). In order to simulate the “worst case” leaching conditions, the semi-dynamic leaching test was modified using 0.014 M acetic acid (pH = 3.25) and humic acids solution (20 mg l^-1 TOC) as leachants instead of deionized water. A diffusion-based model was used to elucidate the controlling leaching mechanisms. Applied treatment was effective in immobilizing cadmium irrespective of high availability in the untreated sample. The controlling leaching mechanism appeared to be diffusion, which indicates that a slow leaching of cadmium could be expected when the cardboard mill sludge as stabilization agent is applied.

The surface of textile materials is highly textured, commonly in non-uniform ways. Because of this texture effect, textile surface appears rougher and more porous than other printing substrates, which can cause excessive ink penetration during printing process. Next, washing process is very important factor because it influences ink characteristics on printed samples as well as structural changes of the textile substrate. The aim of this paper is to determine the influences of washing process and different mesh tread count used for printing on print quality. This will be obtained by using spectrophotometric analysis, and GLCM image processing method for print mottle estimation. The results of this research show that increasing number of washing processes leads to higher color differences reproduction color in comparison to printed materials before washing. It also shows that textile surface texture has a great influence on print mottle as well as that number of washing treatment series can generate variations of solid-tone print uniformity.

During exploitation, textile products printed with screen printing technique are quite often exposed to various influences, one of which is a heat treatment- firstly during the production process and later on when ironing. Heat is simultaneously affecting deposited colorants (ink) on the surface of the substrate material, as well as textile fibers in the material structure. As a result, colorimetric characteristics of printed colorants are changed. The research presented in this paper aims to determine the influence of heat treatment on color changes of screen printed textile substrates, observed in CIE L*, a*, b* color space. Macro non-uniformity of the printed cotton textile materials was analyzed as a function of temperature levels applied during thermal treatments and textile material characteristics, as well as mesh counts of screens used in the printing process. The results show that thermal treatment affects the color change of printed samples.