Nanoemulsion technique, based on Ouzo effect, was applied for synthesis of the pure and silver doped (2.5 and 5mol%) calcium hydroxyapatite (HAp). After calcination at 500?C fully crystallized powders were obtained. X-ray powder diffraction analysis accompanied with Rietveld refinement revealed that the synthesized powders were single-phase hydroxyapatite. Raman spectroscopy also confirmed that the synthesized powders were single-phase. The obtained HAp particles were spherical in shape and their sizes were in the nanometer range which was revealed by field emission scanning electron microscopy analysis (FESEM). The successful synthesis of the single-phase Ag doped HAp showed that nanoemulsion method is a simple technique for obtaining pure and doped hydroxyapatite nanospheres.

Sphene based glass-ceramics (CaTiSiO5), an excellent candidate for a host lattice of ceramic materials and for nuclear waste immobilization, has been prepared from a powder mixture of CaCO3, TiO2 and SiO2 using vibro-milling for homogenization. Starting powders were melted at 1400?C for 2 h, cooled to room temperature, grounded again, then crystallized by thermal treatment yielding a sphene glass-ceramic. The evolution of the phase composition during thermal treatment was investigated by X-ray powder diffraction (XRPD), FT-IR, Raman and thermal analyses (TG-DTA). Pure synthetic single phase sphene was formed at 800?C for 4 h, even it is very hard to obtain monophase powder at such low temperature. Powder morphology was analyzed by scanning electron microscopy (SEM).