The phase composition of self-healing products generated in cracks affects self-healing performance. This study investigated the self-healing products of cementitious materials using supplementary cementitious materials (SCMs), a calcium sulfoaluminate (CSA) expansion agent, and crystalline additives (CAs). Ground-granulated blast-furnace slag (GGBFS), fly ash (FA), and silica fume (SF) were used as SCMs, and anhydrite, Na₂SO₄, Na₂CO₃, and MgCO₃ were used as crystalline additives (CAs). An artificial crack method was used to collect the self-healing products in the crack of the paste. The phase composition of the self-healing products was analyzed through X-ray diffraction (XRD)/Rietveld refinements and thermogravimetry/differential thermogravimetry (TG/DTG) analysis, and their morphology and ion concentration were examined through scanning electron microscopy with energy dispersive spectroscopy (SEM–EDS). From the results, the main compound of self-healing products was found to be calcite. GGBFS and FA decreased the content of portlandite, and the use of CAs led to the formation of alkali sulfate and alkali carbonate. The SEM–EDS analysis results showed that when GGBFS and FA were used, a large proportion of the self-healing products contained C-S-H and C-A-H, and the use of CSA led to the formation of monosulfate and ettringite.

In this study, the effect of carbon nanotubes (CNTs) on the physical properties of cement composites was investigated. The mechanism of the change of autogenous shrinkage of CNTs-reinforced cement composites was also examined. In the experiments, ordinary Portland cement (OPC) and fly ash (FA) were used as binders, and 0.0, 0.1, 0.3, and 0.5% multi-walled CNTs (MWCNTs) were added to fabricate pastes. When the hydration heat was measured through isothermal calorimetry, it was found that CNTs accelerated the early age hydration of the pastes and that the hydration rate increased as the CNT content increased. The compressive strength was the highest when the CNT content was 0.1%. As the CNT content increased, the internal relative humidity (IRH) decreased and autogenous shrinkage showed a decreasing tendency. Through the analysis of the correlation between autogenous shrinkage and IRH, it was confirmed that the reduction in autogenous shrinkage due to the addition of CNTs resulted from the decrease in bulk strain.

In this study, the physical and durability properties of cementitious materials containing stainless steel argon-oxygen decarburization (AOD) slag were investigated by CO₂ curing. Three contents (0, 30, 60%) of ordinary Portland cement (OPC) were replaced with AOD slag. Specimens were cured at four CO₂ concentrations and three temperatures. The chloride diffusion coefficient, drying shrinkage, compressive strength, and porosity were measured. The drying shrinkage reduction was proportional to CO₂ uptake. The chloride diffusion coefficient increased as contents of the AOD slag increased. At 15% CO₂ concentration, the diffusion coefficient was similar to that of the OPC regardless of the AOD slag substitution rate. The durability of cementitious materials mixed with AOD slag can be improved by CO₂ curing and can be used in construction.