The behaviour of reinforced concrete frames with masonry wall infills is influenced a lot by the stiffness and strength difference between the frame and the infill, causing early detrimental damage to the infill or to the critical concrete columns. The paper reports the results from shake table seismic tests on a full-scale reinforced concrete (RC) frame building with modified hollow clay block (orthoblock brick) infill walls, within INMASPOL SERA Horizon 2020 project. The building received innovative resilient protection using Polyurethane Flexible Joints (PUFJs) made of polyurethane resin (PU), applied at the frame-infill interface in different schemes. Further, PUs were used for bonding of glass fibre grids to the weak masonry substrate to form Fibre Reinforced Polyurethanes (FRPUs) as an emergency repair intervention. The test results showed enhancement in the in-plane and out-of-plane infill performance under seismic excitations. The results confirmed remarkable delay of significant infill damages at very high RC frame inter-story drifts as a consequence of the use of PUFJs. Further, the PUFJ protection enabled the resilient repair of the infill even after very high inter-story drift of the structure up to 3.7%. The applied glass FRPU system efficiently protected the damaged infills against collapse under out-of-plane excitation while they restored large part of their in-plane stiffness.

This paper presents the results of direct tensile tests performed on six different FRCM (fabric reinforced cementitious matrix) strengthening systems used for masonry structures. The emphasis was placed on the determination of the mechanical parameters of each tested system and a comparison of their tensile behaviour in terms of first crack stress, ultimate stress, ultimate strain, cracking pattern, failure mode and idealised tensile stress-strain curve. In addition to the basic mechanical tensile parameters, accidental load eccentricities, matrix tensile strengths, and matrix modules of elasticity were estimated. The results of the tests showed that the tensile behaviour of FRCM composites strongly depends on the parameters of the constituent materials (matrix and fabric). In the tests, tensile failure of reinforcement and fibre slippage within the matrix were observed. The presented research showed that the accidental eccentricities did not substantially affect the obtained results and that the more slender the specimen used, the more consistent the obtained results. The analysis based on a rule of mixtures showed that the direct tensile to flexural tensile strength ratio of the matrixes used in the test was 0.2 to 0.4. Finally, the tensile stress–strain relationship for the tested FRCMs was idealised by a bi- or tri-linear curve.

This paper investigates composite-to-brick strengthening systems with flexible adhesive made of polyurethane (Carbon Fibre Reinforced Polyurethane (CFRPU) and Steel Reinforced Polyurethane (SRPU)) and epoxy resin (Carbon Fibre Reinforced Polymer (CFRP) and Steel Reinforced Polymer (SRP). The specimens were tested in a single lap shear test (SLST). LVDT displacement transducers (LVDT – Linear Variable Differential Transformer) and digital image correlation method (DIC) based measurement systems were used to measure displacements and strains. The obtained results were applied in a numerical analysis of the 3D model of the SLST specimen, with flexible adhesives modeled as a hyper-elastic model. The DIC and LVDT based systems demonstrated a good correlation. Experimental and numerical analysis confirmed that composite-to-brick strengthening systems with flexible adhesives are more effective on brittle substrates than stiff ones, as they are able to reduce stress concentrations and more evenly distribute stress along the entire bonded length, thus having a higher load carrying capacity.