The current paper studies the influence of geometrical parameters of the fused deposition modeling (FDM)—fused filament fabrication (FFF) 3D printing process on printed part strength for open source desktop 3D printers and the most popular material used for that purpose—i.e., polylactic acid (PLA). The study was conducted using a set of different nozzles (0.4, 0.6, and 0.8 mm) and a range of layer heights from the minimum to maximum physical limits of the machine. To assess print strength, a novel assessment method is proposed. A tubular sample is loaded in the weakest direction (across layers) in a three-point bending fixture. Mesostructure evaluation through scanning electronic microscopy (SEM) scans of the samples was used to explain the obtained results. We detected a significant influence of geometric process parameters on sample mesostructure, and consequently, on sample strength.

The ability to form closed cavities inside the part printed is an important feature of Fused Filament Fabrication technology. A typical part consists of a dense shell bearing the primary load, filled with low-density plastic scaffold (infill). Such a constitution of the part provides in most cases appropriate strength and low weight. However, if the printed part shape includes horizontal (orthogonal to printer’s Z axis) flat surfaces other than its top and bottom surface, then the shell of the part becomes interrupted, which may lead to drastic drop in the ability of the part to withstand loads. In the current study, a representative sample of a part with interrupted shell and testing apparatus is developed. Influence of shell and base thicknesses, as well as influence of the infill density on the part strength, are studied. Different approaches to the sample shape modification were applied and tested. The part shape optimization made with respect to peculiarities of Fused Filament Fabrication technology resulted in increment of the force, required to fracture the part from 483 to 1096 N and in decreased part mass from 36.9 to 30.2 g.

The current study aims to evaluate the possibilities to increase part strength by optimizing the Fused Filament Fabrication (FFF) process parameters. Five different CAD models of parts with the same coupling dimensions but of different shape inherited from a recent study were converted into test samples with Ultimaker 2 3D printer. The main measure of success was the sample strength, defined as the load at which the first crack in the stressed area of the part appeared. Three different modifications to the FFF process with verified positive effect on interlayer bonding were applied. The first modification included raising the extrusion temperature and disabling printed part cooling. The second modification consisted of reduction in the layer thickness. The third modification combined the effects of the first and the second ones. For four out of five shapes tested the applied process modifications resulted in significant strengthening of the part. The shape that exhibited the best results was subject to further research by creating special printing mode. The mode included fine-tuning of three technological parameters on different stages of the part fabrication. As a result it was possible to increase the part strength by 108% only by tuning printing parameters of the best shape designed with increasing its weight by 8%.