Aldol condensation reactions between furfural and acetone can be used to produce liquid fuel intermediates. It was found that tin-containing zeolites with MFI (Sn-MFI) and BEA* (Sn-Beta) framework structures are effective for C–C bond formation via the aldol condensation reactions between furfural and acetone. Aldol condensation between furfural and acetone produced two main products, 4-(2-furyl)-3-buten-2-one (FAc) and 1,5-di-2-furanyl-1,4-pentadien-3-one (F₂Ac). Although both these catalysts were active for the aldol condensation reactions, different selectivities to aldol products were observed over Sn-MFI and Sn-Beta. FAc and F₂Ac were formed over the Sn-Beta catalyst with selectivities to FAc of 40% and F₂Ac of 22%, respectively. In contrast, only FAc was produced over Sn-MFI. The variation in selectivity is likely due to different pore geometries of Sn-Beta and Sn-MFI, suggesting that Sn-MFI exhibits shape selectivity for aldol condensation between furfural and acetone. In addition, it was found that the addition of water to the reaction system can also affect the product selectivity, leading to the aldol product exclusively being FAc over Sn-Beta.

In this work, glucose was transformed into 5-hydroxymethylfurfural (HMF) and 5-ethoxymethylfurfural (EMF) in the presence of AlCl ₃ ·6H ₂ O and a Brønsted solid acid catalyst (PTSA–POM).

A resorcinol-formaldehyde resin carbon (RFC) catalyst with a well-developed, ordered, mesoporous framework was prepared using a soft template method at room temperature. The carbon was sulfonated in water using sulfanilic acid under mild atmospheric conditions. The sulfonated RFC (S-RFC) was characterized by N₂ adsorption–desorption, elemental analysis, TEM, XPS, and FT-IR. It was determined that S-RFC is an efficient solid acid catalyst for furfural production from xylose and corn stover in γ-valerolactone (GVL). The effects of reaction time, reaction temperature, catalyst loading, substrate dosage and water concentration were investigated. 80% furfural yield and 100% xylose conversion were obtained from xylose at 170 °C in 15 min with 0.5 g catalyst. Comparatively, 68.6% furfural yield was achieved from corn stover at 200 °C in 100 min when using 0.6 g catalyst. Since there was no discernable decrease in furfural yield after multiple conversions utilizing the same catalyst, the recyclability of the catalyst is considered good.

A novel solid p-hydroxybenzenesulfonic acid–formaldehyde resin (SPFR) was prepared via a straightforward hydrothermal method. The catalytic properties of SPFR solid acids were evaluated in the dehydration reaction of fructose and glucose to 5-hydroxymethylfurfural (HMF). SEM, TEM, N₂ adsorption–desorption, elemental analysis (EA), thermogravimetric analysis (TGA), and FT-IR were used to explore the effects of catalyst structure and composition on the HMF preparation from fructose. The effects of reaction time and temperature on the dehydration of fructose and glucose were also investigated. An HMF yield as high as 82.6% was achieved from fructose at 140 °C after 30 min, and 33.0% was achieved from glucose at 190 °C in 30 min. Furthermore, the recyclability of SPFR for the HMF production from fructose in 5 cycles was good.