The introduction of resin-based cements and an adhesive-bonding system in daily dental practice has given the opportunity to increase the retention of previously conventional cemented restorations and the optimal results in esthetic. This experimental study employed the 3D Digital Image Correlation Method (3D-DIC) for detecting shrinkage strain in four dual cured composite cements. The aim was to visualize measure, analyze, and compare strain fields in four resin-based cements using the 3D-DIC method. A total of 72 samples were divided into 4 groups considering variations in sample types, diameter, and thickness. Four types of composite cements: RelyX U200 (3 M ESPE, St. Paul, MN, USA), MaxCem Elite (Kerr, Orange, CA, USA), Multilink Automix (Ivoclar Vivadent, Schaan, Liechtenstein), and SeT PP (SDI, Australia) were used. Each type had diameters of 3 mm, 4 mm, and 5 mm, respectively, combined with two different values of thickness: 1 mm and 2 mm. Thickness had an important role on strain detected in all tested materials showing higher strain in samples with 2 mm thickness compared to 1 mm samples. Shrinkage strain values were the highest in Set PP samples indicated the possibility of undesirable de-bonding.

Introduction/Objective. In an attempt to simplify dental procedures, a new group of resin cements, self-adhesive resin cements (SARCs), have been introduced. Performance of SARCs can widely vary. One of the main reasons of adhesion failure is polymerization shrinkage. The aim of this study was to determine, evaluate, and measure strain field of self-adhesive dual cure resin cement during polymerization in self-cure mode using 3D digital image correlation (DIC) method. Methods. The self-adhesive Maxcem Elite (Kerr, Orange, CA, USA) cement was tested in five cylindrical samples (5 mm in diameter and 2 mm in thickness) prepared by filling plastic ring-type molds. Digital images were recorded immediately after sample preparation. Results. Non-uniform strain distribution was found in resin cement with higher strain values along the periphery (up to 15%) and lower strain values in central parts (around 4%) of each sample. Conclusion. It can be concluded that DIC is a powerful tool for full-field strain measurements in material characterization.

This study aimed to assess the effectiveness of various combinations of the implant-supported overdentures and removable partial dentures on nutritional status in a randomized sample of 150 older adults. The body mass index (BMI) and the Mini Nutritional Assessment (MNA) were recorded before and after prosthetic rehabilitation. There was statistically significant improvement in the MNA and BMI, measured before prosthetic rehabilitation, and after 6 and 12 months (P < .001). The prosthetic rehabilitation of patients 65 years and older, using implant-supported overdentures and removable partial dentures, improved BMI and MNA scores used in the assessment of nutritional status.

The study showed an application of the 3 D Digital Image Correlation Method (3 D-DIC) for detection of von Mises strain in samples of the self-etch, self-adhesive resin based cement (RBC). The aim was to determine and compare strain in the self-cured and light-cured Maxcem Elite, furthermore to investigate the hardness of these two cement-types. The experiment was carried out using two groups of Maxcem Elite (Kerr, Orange, CA, USA) samples; each tested group includes five (ø5 × 2 mm sized) samples, for both self-curing and light-curing mode. All samples were prepared by filling teflon ring-type molds. In addition, Vickers micro-hardness was measured for all samples. Maxcem Elite showed similar maximum strain values from 10% to 12% for both groups. Besides the maximum strain value, the 3 D-DIC method also enabled monitoring the change of strain field even after the recommended polymerization time. This method has shown that the polymerization shrinkage continues even after 10 min which disagreed with manufacturer’s suggestion. Group II showed maximum strain values of 12% in the peripheral zone after 10 min, in the last Stage (Stage 60). Statistically significant difference was not found in the overall strain between self- and light-cured Maxcem Elite neither peripherally (p = 0.118) nor centrally (p = 0.879). However, statistical significance was found in strain regarding central and peripheral zone in both, self-cured (p = 0.020) and light-cured (p = 0.002) Maxcem Elite. The mean von Mises strain values in the periphery of the samples (Section 0) were significantly higher compared to strain values in the center of the samples (for Section 1 and 2). The last stage (Stage 60) of the light-cured Maxcem Elite polymerization showed significantly higher values of von Mises strain compared to initial stage (Stage 0). Higher values of micro-hardness were noticed on the surfaces directly exposed to LED lamp after performing measurements of micro-hardness on light-cured samples.