Polymer adhesives play an important role in many medical, consumer, and industrial products. Polymers of α-lipoic acid (αLA) have the potential to fulfill the need for versatile and environmentally friendly adhesives, but their performance is plagued by spontaneous depolymerization. We report a family of stabilized αLA polymer adhesives that can be tailored for a variety of medical or nonmedical uses and sustainably sourced and recycled in a closed-loop manner. Minor changes in monomer composition afforded a pressure-sensitive adhesive that functions well in dry and wet conditions, as well as a structural adhesive with strength equivalent to that of conventional epoxies. αLA surgical superglue successfully sealed murine amniotic sac ruptures, increasing fetal survival from 0 to 100%.

In this work, a recycling and self-healing strategy for polybenzoxazines through both S–S bond cleavage-reformation reaction and supramolecular attractions is described. Both recyclable and self-healable polybenzoxazines can be prepared from low cost chemicals with a simple procedure in only 30 minutes. For this purpose, inverse vulcanization of poly(propylene oxide)benzoxazine (PPOB) and diallybenzoxazine (B-al) with elemental sulfur was performed at 185 °C. The obtained cross-linked polymer films exhibited thermally driven recycling ability up to 5 cycles. Moreover, the self-healing ability of a test specimen was shown. Spectral characterizations, thermal stability and fracture toughness of the films were investigated after each recycling.