Among corrosive environments, Cl⁻ is one of the most aggressive anions which can cause electrochemical corrosion and the resultant failures of alloys, and the increase in Cl⁻ concentration will further deteriorate the passive film in many conventional alloys. Here, we report single-phase Nb₂₅Mo₂₅Ta₂₅Ti₂₀W₅C_x (x = 0.1, 0.3, 0.8 at.%) refractory high-entropy alloys (RHEAs) with excellent corrosion resistance in high-concentration NaCl solutions. According to potentiodynamic polarization, electrochemical impedance spectroscopy, corroded morphology and the current–time results, the RHEAs demonstrate even better corrosion resistance with the increase in NaCl concentration to 23.5 wt.%, significantly superior to 304 L stainless steel. Typically, the corrosion current density (i_corr) and over-passivation potential (E_t) reached the lowest and highest value, respectively, in the 23.5 wt.% NaCl solution, and the i_corr (2.36 × 10⁻⁷ A/cm²) of Nb₂₅Mo₂₅Ta₂₅Ti₂₀W₅C_0.1 alloy is nearly two orders lower than that of 304 L stainless steel (1.75 × 10⁻⁵ A/cm²). The excellent corrosion resistance results from the formation of passive films with fewer defects and more stable oxides. Moreover, with the addition of the appropriate C element, the RHEAs also demonstrated improved strength and plasticity simultaneously, for example, the Nb₂₅Mo₂₅Ta₂₅Ti₂₀W₅C_0.3 alloy exhibited an average yield strength of 1368 MPa and a plastic strain of 19.7%. The present findings provide useful guidance to address the conflict between the excellent corrosion resistance and high strength of advanced alloys.

Refractory high-entropy alloys (RHEAs) are categorized as difficult-to-machine materials due to their excellent mechanical properties. Electrical discharge machining (EDM) is a special processing method for RHEAs, which faces challenges such as low machining efficiency. In this work, electrochemical discharge machining (ECDM) was proposed for (TiVZrTaW)_99.5N_0.5 and (TiVZrTa)W₅ (at. %, denoted as W20N0.5 and W5, respectively) RHEAs, and their machining performances were investigated and compared with EDM. At a peak current of 25 A, the material removal rate (MRR) using ECDM is more than twice that of EDM for W20N0.5 (reaching to 1.24 mm³/min) and 1.5 times higher than that for W5. Both W20N0.5 and W5 RHEAs exhibited higher MRR in ECDM based on the analyses of the influence of top diameter, bottom diameter, machining depth, and surface roughness (Ra). The process and mechanisms of material removal were examined through the microstructural morphology and elemental distribution analyses. This work proposed a more effective route for machining RHEAs by ECDM compared to the conventional EDM.