Herein, ZIF-8 inorganic particles with different sized reinforced poly (vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) solid composite polymer electrolytes (PVDF-HFP/10%ZIF-8) were prepared via a facile blade-coating approach, and free-standing quasi solid-state composite electrolytes (PVDF-HFP/10%ZIF-8(0.6)/Plasticizer, abbreviated as PH/10%ZIF-8(0.6)/P), were further obtained through the introduction of plasticizer. Optimized PH/10%ZIF-8(0.6)/P exhibited a high ionic conductivity of 2.8 × 10⁻⁴ S cm⁻¹ at 30 °C, and superior Li⁺ transfer number of 0.89 with an ultrathin thickness (26 µm). Therefore, PH/10%ZIF-8(0.6)/P could effectively inhibit the growth of lithium dendrites, and the assembled Li/LiFePO₄ cell delivered good cycling stability with a capacity retention rate of 89.1% after 100 cycles at 0.5 C.

Developing an advanced electrode structure is highly important for obtaining lithium sulfur (Li–S) batteries with long life, low cost, and environmental friendliness. Some bottlenecks, such as large volume deformation and environmental pollution caused by the electrode preparation process, are still hindering the practical application of Li–S batteries. In this work, a new water-soluble, green, and environmentally friendly supramolecular binder (HUG) is successfully synthesized by modifying natural biopolymer (guar gum, GG) with HDI-UPy (cyanate containing pyrimidine groups). HUG can effectively resist electrode bulk deformation through a the unique three-dimensional nanonet-structure formed via covalent bonds and multiple hydrogen bonds. In addition, abundant polar groups of HUG have good adsorption properties for polysulfide and can inhibit the shuttle movement of polysulfide ions. Therefore, Li–S cell with HUG exhibits a high reversible capacity of 640 mAh g⁻¹ after 200 cycles at 1C with a Coulombic efficiency of 99%.

Compared to traditional liquid electrolytes, solid electrolytes have received widespread attention due to their higher safety. In this work, a vinyl functionalized metal–organic framework porous material (MIL-101(Cr)-NH-Met, noted as MCN-M) is synthesized by postsynthetic modification. A novel three-dimensional hybrid gel composite solid electrolyte (GCSE-P/MCN-M) is successfully prepared via in situ gel reaction of a mixture containing multifunctional hybrid crosslinker (MCN-M), lithium bis(trifluoromethanesulfonyl)imide (LiTFSI), ethylene carbonate (EC), diethylene glycol monomethyl ether methacrylate (EGM) and polyethylene (vinylidene fluoridee) (PVDF). Benefiting from the excellent mechanical properties, rich pore structure, and numerous unsaturated metal sites of GCSE-P/MCN-M, our GCSE-P/MCN-M exhibits excellent mechanical modulus (953 MPa), good ionic conductivity (9.3 × 10⁻⁴ S cm⁻¹) and wide electrochemical window (4.8 V). In addition, Li/LiFePO₄ batteries based on GCSE-P/MCN-M have also demonstrated excellent cycling performance (a high-capacity retention of 87% after 200 cycles at 0.5 C). This work provides a promising approach for developing gel solid-state electrolytes with high ion conduction and excellent safety performance.

A Yb³⁺-doped BiOI 3D nanosheet array composite was successfully fabricated through a solvothermal deposition strategy on flexible carbon cloth (CC). This composite was subsequently integrated with high-chlorine fly ash (FA) blocks to form the Yb-BiOI/CC/FA hybrid material. Comprehensive characterization was performed using multiple analytical techniques for crystalline phase identification, morphological analysis, valence state, band structure evaluation, and charge carrier separation assessment. Electrochemical measurements were conducted to evaluate the material’s electronic properties. Experimental results demonstrated superior photocatalytic performance under visible light irradiation, with the Yb-BiOI/CC/FA composite achieving 52.87% methylene blue degradation efficiency. The reaction rate constant of this modified nanomaterial was approximately 2.1 times higher than that of pristine BiOI/CC/FA. Radical trapping experiments revealed that superoxide radicals (·O₂⁻) served as the predominant oxidative species. This study presents a dual-benefit strategy for environmental remediation by simultaneously achieving sustainable waste valorization of industrial byproducts (FA) and developing high-efficiency photocatalytic materials. The successful integration of rare-earth metal modification with substrate engineering provides valuable insights for designing advanced photocatalytic systems for pollutant degradation.