Utilizing solid particles as a heat-transfer medium in concentrated solar power applications has gained growing attention lately. Unlike molten salts, solid particles offer many benefits, which include: high operating temperatures (greater than 1000 °C), a lack of freezing issues and corrosivity, abundant availability, high thermal energy storage capacity, a low cost, and applicability in direct irradiation. Comprehensive knowledge of thermophysical and optical properties of solid particles is essential to ensure an effective harnessing of solar energy. The most important considerations when selecting solid particles include: thermophysical and optical properties, thermal resistance, crack resistance, satisfactory health and safety risks, availability, and low cost. It is also imperative to consider optical and thermophysical characteristics that might change from what they were “as received” after cyclic heating for a long period. Therefore, the knowledge of thermal performance of particulate materials becomes significant before using them as a heat-transfer medium. In this study, some particulate materials were chosen to study their feasibilities as heat-transfer and storage media for a particle-based central receiver tower system. These particulate materials included white sand, red sand, ilmenite, and Carbobead CP. The candidate particulate materials were heated at high temperatures for 6 h and then cooled to room temperature. After that, cyclic heating was performed on the particulate materials for 500 h at 1200 °C. The optical properties were represented by weighted solar absorptance, and the thermophysical properties of the particulates were measured “as received” and after cyclic heating (aging). EDX and XRD were conducted to quantify the chemical composition and interpret the changes in appearance associated with the particulate materials after cyclic heating. The results showed a considerable agglomeration in all particulates except for white sand in the 6 h heating test, and high agglomeration in the ilmenite. A slight decrease in the optical properties in the white sand and Carbobead CP was found after the aging test. The specific heat was decreased for red and white sand. The EDX and XRD results for white sand and Carbobead CP showed chemical stability, indicating high durability and reliability.

Tests were performed at the particle-based CSP test facility at King Saud University to demonstrate a viable solution to overcome the limitations of using molten salt as a working medium in power plants. The KSU facility is composed of a heliostat field, particle heating receiver (PHR) at the top of a tower, thermal energy storage (TES) bin, a particle-to-working fluid heat exchanger (PWFHX), power cycle (microturbine), and a particle lift. During pre-commissioning, a substantial portion of the collected solar energy was lost during particle flow through the TES bin. The entrained air is shown to be the primary cause of such heat loss. The results show that the particle temperature at the PHR outlet can reach 720 °C after mitigating the entrained air issue. Additionally, during on-sun testing, a higher temperature of the air exiting the PWFHX than that of the air entering is observed, which indicates the effective solar contribution. Half-hour plant operation through stored energy was demonstrated after heliostat defocusing. Lastly, a sealable TES bin configuration for 1.3 MWe pre-commercial demonstration unit to be built in Saudi Arabia by Saudi Electric Company (SEC) is presented. This design modification has addressed the heat loss, pressure build-up, and contamination issues during TES charging.

Using solid particulates as a heat transfer medium for concentrated solar power (CSP) systems has many advantages, positioning them as a superior option compared with conventional heat transfer media such as steam, oil, air, and molten salt. However, a critical imperative lies in the comprehensive evaluation of the properties of potential solid particulates intended for utilization under such extreme thermal conditions. This paper undertakes an exhaustive examination of both ambient and high-temperature thermophysical properties of four naturally occurring particulate materials, Riyadh white sand, Riyadh red sand, Saudi olivine sand, and US olivine sand, and one well-known engineered particulate material. The parameters under scrutiny encompass loose bulk density, tapped bulk density, real density, sintering temperature, and thermal conductivity. The results reveal that the theoretical density decreases with the increase in temperature. The bulk density of solid particulates depends strongly on the particulate size distribution, as well as on the compaction. The tapped bulk density was found to be larger than the loose density for all particulates, as expected. The sintering test proved that Riyadh white sand is sintered at the highest temperature and pressure, 1300 °C and 50 MPa, respectively. US olivine sand was solidified at 800 °C and melted at higher temperatures. This proves that US olivine sand is not suitable to be used as a thermal energy storage and heat transfer medium in high-temperature particle-based CSP systems. The experimental results of thermal diffusivity/conductivity reveal that, for all particulates, both properties decrease with the increase in temperature, and results up to 475.5 °C are reported.