The direct reductive amination of carbonyl compounds with NH3 and H2 is an alternative route to produce primary amines in practical production. The search for efficient and selective catalysts has attracted great interest. In the present work, the reductive amination of heptaldehyde with NH3 was investigated over a Ru-based catalyst. The product selectivities were found to be related with the supports of Ru. The alumina with spinel structure (γ-Al2O3, θ-Al2O3)-supported Ru catalysts exhibited selectivity favoring primary amines (94% yield) at 100% heptaldehyde conversion under optimal conditions. Purely basic (MgO, CaO) and relative acidic (Nb2O5, SnO2, MCM-41, HZSM-5) supports showed relatively poor selectivity towards primary amines (0%–53% yield). The reductive amination mechanism was also proposed. The Schiff base N-[heptylene]heptyl-1-amine was a key intermediate. Ru/γ-Al2O3 was shown to be an excellent hydrogenolysis catalyst to selectively produce primary amine by amination and hydrogenolysis of N-[heptylene]heptyl-1-amine.

Co-Ni catalysts, prepared by a typical wetness impregnation method, can selectively convert furfural (FFA) to cyclopentanone (CPO) or cyclopentanol (CPL) in water, respectively. The catalytic performance depends strongly on the support. It is also strongly influenced by the Co-Ni loadings of the catalyst. The 10%Co-10%Ni/TiO₂ catalyst showed the highest selectivity toward CPO (53.3%) with almost complete FFA conversion, and the main product was CPL (45.4%) over 20%Co/TiO₂ at the optimized conditions (150 °C, 4 MPa H₂, 4 h). The surface morphology, surface area, composition and reducibility properties of these catalysts were fully characterized by XRD, H₂-TPR, ICP-AES and SEM. The factors that influenced the activity of catalysts were also investigated in detail. Additionally, the stability of catalyst for the hydrogenative rearrangement of FFA was studied.

The exploitation of highly efficient solvent-free catalytic systems for the selective aerobic oxidation of benzylic compounds to produce corresponding ketones with molecular oxygen under mild conditions remains a great challenge in the chemical industry. In this work, Au-Pd nanoparticles supported on porous carbon catalysts were fabricated by the borax-mediated hydrothermal carbonization method and the chemical reduction method. The physicochemical properties of Au-Pd bimetallic samples were examined by XRD, N₂ sorption, SEM, TEM, and XPS techniques. The Au-Pd nanoparticles have successfully immobilized on the spherical carbon support with a porous structure and large surface area. A solvent-free catalytic oxidation system was constructed to selectively convert indane into indanone with Au-Pd nanocatalysts and O₂. In contrast with a monometallic Au or Pd catalyst, the resulting bimetallic Au-Pd catalyst could effectively activate O₂ and exhibit improved catalytic activity in the controlled oxidation of indane into indanone under 1 bar O₂. A total of 78% conversion and >99% selectivity toward indanone can be achieved under optimized conditions. The synergistic effect of Au and Pd and porous carbon support contributed to the high catalytic activity for aerobic benzylic compound oxidation. This work offers a promising application prospect of efficient and recyclable Au-Pd nanocatalysts in functional benzylic ketone production.