Precision edge preparation techniques for cemented carbides enable optimization of the geometry of tools’ cutting edges. These techniques are frequently used in high-stress environments, resulting in substantial improvements in tools’ cutting performance. This investigation examined the impact and evolution of cutting edge parameters and resulting surface finishes as a function of dry-electropolishing time on an end-mill. Findings demonstrate enlargement of the cutting edge radius, a decrease in surface roughness, and the mitigation of defects induced during previous manufacturing stages (i.e., smashed ceramic particles, burrs, chipping, etc.). Additionally, a direct correlation between dry-electropolishing time and primary cutting edges’ micro-geometry parameters has been established.

Post-processing, and particularly the dry electropolishing process, is essential for improving the surface quality of 3D-printed Ti6Al4V samples, with specific emphasis on reducing roughness over extended polishing times while preserving mechanical properties. Reducing surface roughness enhances the reliability of hardness measurements and improves the consistency of elastic modulus measurements, as prolonged polishing time stabilizes the full width at half maximum values, thereby minimizing variability due to uniaxial indentation. This stability is crucial for maintaining the structural integrity and uniformity of mechanical properties, facilitating better performance and reliability in biomedical applications. Additionally, under service-like working conditions, solid electrolyte particles undergo dehydration due to the Joule effect, introducing a dynamic aspect to the system as the particle structure degrades with thermal cycling. EDX cross-sectional analysis reveals that TiO₂ informs the particle’s surface, with an oxygen-to-titanium ratio that confirms the oxide’s composition. This TiO₂ oxide layer demonstrates the progressive surface oxidation occurring under the post-processing process, further modifying the particle’s surface chemistry. This dual effect of roughness reduction and controlled surface chemistry highlights the role of dry electropolishing in enhancing the functional lifespan and mechanical reliability of Ti6Al4V components.

This study investigates the thermal stability and microstructural evolution of the solid electrolyte medium used in DLyte^® dry electropolishing and dry anodizing processes. Samples were thermally aged between 30 °C and 45 °C to simulate Joule heating during industrial operation. Visual and SEM analyses revealed shape deformation and microcrack formation at temperatures above 40 °C, potentially reducing particle packing efficiency and electrolyte performance. Particle size distribution shifted from bimodal to trimodal upon aging, with an overall size reduction of up to 39.5% due to dehydration effects, impacting ionic transport properties. Weight-loss measurements indicated a diffusion-limited dehydration mechanism, stabilizing at 15–16% mass loss. Fourier transform infrared analysis confirmed water removal while maintaining the essential sulfonic acid groups responsible for ionic conductivity. In dry anodizing tests on titanium, aged electrolytes enhanced process efficiency, producing TiO₂ films with improved optical properties—color and brightness—while preserving thickness and uniformity (~70 nm). The results highlight the need to carefully control thermal exposure to maintain electrolyte integrity and ensure consistent process performance.