Reversibly intercalating ions into host materials for electrochemical energy storage is the essence of the working principle of rocking-chair type batteries. The most relevant example is the graphite anode for rechargeable Li-ion batteries which has been commercialized in 1991 and still represents the benchmark anode in Li-ion batteries 30 years later. Learning from past lessons on alkali metal intercalation in graphite, recent breakthroughs in sodium and potassium intercalation in graphite have been demonstrated for Na-ion batteries and K-ion batteries. Interestingly, some significant differences proved to exist for the intercalation of Na⁺ and K⁺ into graphite compared with the Li⁺ case. Such different host–guest interactions are unique depending on the host materials and electrolytes, which greatly contribute to a deeper understanding of intercalation-type electrode materials for next generation alkali metal ion batteries. This review summarizes significant advances from both experimental and theoretical calculations with a focus on comparing the intercalation of three alkali metal ions (Li⁺, Na⁺, K⁺) into graphite and aims to clarify the intimate host–guest relationships and the underlying mechanisms. New approaches developed to achieve favorable intercalation coupled with the challenges in this field are also discussed. We also extrapolate alkali metal ion intercalation in graphite to mono-/multi-valent ions in layered electrode materials, which will deepen the understanding of intercalation chemistry and provide guidance to explore new guests and hosts.

Li and Mn‐rich layered oxides, xLi₂MnO₃·(1–x)LiMO₂ (M=Ni, Mn, Co), are promising cathode materials for Li‐ion batteries because of their high specific capacity that can exceed 250 mA h g⁻¹. However, these materials suffer from high 1^st cycle irreversible capacity, gradual capacity fading, low rate capability, a substantial charge‐discharge voltage hysteresis, and a large average discharge voltage decay during cycling. The latter detrimental phenomenon is ascribed to irreversible structural transformations upon cycling of these cathodes related to potentials ≥4.5 V required for their charging. Transition metal inactivation along with impedance increase and partial layered‐to‐spinel transformation during cycling are possible reasons for the detrimental voltage fade. Doping of Li, Mn‐rich materials by Na, Mg, Al, Fe, Co, Ru, etc. is useful for stabilizing capacity and mitigating the discharge‐voltage decay of xLi₂MnO₃·(1–x)LiMO₂ electrodes. Surface modifications by thin coatings of Al₂O₃, V₂O₅, AlF₃, AlPO₄, etc. or by gas treatment (for instance, by NH₃) can also enhance voltage and capacity stability during cycling. This paper describes the recent literature results and ongoing efforts from our groups to improve the performance of Li, Mn‐rich materials. Focus is also on preparation of cobalt‐free cathodes, which are integrated layered‐spinel materials with high reversible capacity and stable performance.