Superconducting bulks can be magnetized to act as powerful permanent magnets; however, for high trapped fields at temperatures below 77 K, bulks have poor thermal stability and are limited by low mechanical strength. The trapped fields reported in this paper are between two stacks of commercial high-temperature superconducting tape each with 120 layers, magnetized by field cooling. 7.34 T was trapped at approximately 4.2 K, the highest field ever achieved for such a sample. The trapped field also continued to increase below 20 K showing high thermal stability, largely due to the silver over-layer which effectively dissipates heat.

In the present study, our emphasis was directed towards the fabrication process of long multi-core superconducting wires, each spanning several hundred meters. These wires feature an in situ MgB₂ core, an ex situ MgB₂ barrier, and a copper shield. The cost-effectiveness of these constituent materials, coupled with a judicious arrangement of internal components, facilitates the utilization of an economical shielding material for the resulting wire. Our ongoing efforts have successfully yielded several hundred-meter-long wire sections possessing favorable superconducting characteristics, making them suitable for self-field applications, such as direct current (DC) power lines.