Poly(lactide-co-glycolide) (PLGA) nanoparticles of different physical characteristics (size, size distribution, morphology, zeta potential) can be synthesized by controlling the parameters specific...

An emulsion evaporation method was used to synthesize spherical poly(DL-lactide-co-glycolide) (PLGA) nanoparticles with entrapped α-tocopherol. Two different surfactants were used: sodium dodecyl sulfate (SDS) and poly(vinyl alcohol) (PVA). For SDS nanoparticles, the size of the nanoparticles decreased significantly with the entrapment of α-tocopherol in the PLGA matrix, while the size of PVA nanoparticles remained unchanged. The polydispersity index after synthesis was under 0.100 for PVA nanoparticles and around 0.150 for SDS nanoparticles. The zeta potential was negative for all PVA nanoparticles. The entrapment efficiency of α-tocopherol in the polymeric matrix was approximately 89% and 95% for nanoparticles with 8% and 16% α-tocopherol theoretical loading, respectively. The residual PVA associated with the nanoparticles after purification was approximately 6% ( w/w relative to the nanoparticles). The release profile showed an initial burst followed by a slower release of the α-tocopherol entrapped inside the PLGA matrix. The release for nanoparticles with 8% α-tocopherol theoretical loading (86% released in the first hour) was faster than the release for the nanoparticles with 16% α-tocopherol theoretical loading (34% released in the first hour).