Purpose: Polymer rapid tooling (PRT) inserts can be used as injection moulding (IM) cavities for prototyping and low volume production but lack the robustness of metal inserts. Metal inserts can withstand high injection pressure and temperature required, whereas PRT inserts may fail under similar parameters. The current method of parameter setting starts with using the highest pressure setting on the machine and then fine-tuning to optimize the process parameters. This method needs modification, as high injection pressures and temperatures can damage the PRT inserts. There is a need for a methodical process to determine the upper limits of moulding parameters that can be used without damaging the PRT inserts. Design/methodology/approach: A case study analysis was performed to investigate the causes of failure in a PRT insert. From this, a candidate set-up process was developed to avoid start-up failure and possibly prolong tool life. This was then tested on a second mould, which successfully avoided start-up failure and moulded 54 parts before becoming unusable due to safety issues. Findings: Process parameters that are critical for tool life are identified as mould temperature, injection pressure, injection speed, hold pressure and cooling time. Originality/value: This paper presents a novel method for setting IM process parameters for PRT inserts. This has the potential to prevent failure at start up when using PRT inserts and possibly extend the operating life of the PRT inserts.

Background: Polymer-based 3D Printed Injection Mould (3DIM) inserts are used as a cost-effective method for low volume injection moulding (50–500 parts). However, abrupt failure leading to a short tool life is a common shortcoming of 3DIM. Need: The underlying causes of raised feature failures on 3DIM are not well known. Failure is commonly attributed to bending or shearing of raised features on the tool. Understanding the causes may help in delaying the failure and increasing tool life. Approach: Tool failure was analysed from a first-principles perspective, using pressure and temperature fields as determined by mould flow simulation. Experimental results were also obtained for two types of tool material (Visijet M3-X and Digital ABS) with polycarbonate (Lexan 943A) as the part material. Findings: Results find against the idea that pin failure in 3DIM tools is caused by bending and shear failures induced by injection pressures. We also conclude that failure of raised features is not necessarily an abrupt failure as mentioned in the literature. Originality: The generally accepted explanation for the failure of raised features in 3DIM tooling is that injection pressures cause bending and shear failure. This paper disconfirms this notion on theoretical and experimental grounds.

Background—Polymer rapid tooling (PRT) inserts for injection molding (IM) are a cost-effective method for prototyping and low-volume manufacturing. However, PRT inserts lack the robustness of steel inserts, leading to progressive deterioration and failure. This causes quality issues and reduced part numbers. Approach—Case studies were performed on PRT inserts, and different failures were observed over the life of the tool. Parts molded from the tool were examined to further understand the failures, and root causes were identified. Findings—Critical parameters affecting the tool life, and the effect of these parameters on different areas of tool are identified. A categorization of the different failure modes and the underlying mechanisms are presented. The main failure modes are: surface deterioration; surface scalding; avulsion; shear failure; bending failure; edge failure. The failure modes influence each other, and they may be connected in cascade sequences. Originality—The original contributions of this work are the identification of the failure modes and their relationships with the root causes. Suggestions are given for prolonging tool life via design practices and molding parameters.

3D Printed Injection Moulds (3DIM), commonly used for low volume production and prototyping purposes, are known to fail abruptly and have a comparatively shorter life than conventional moulds. Investigating the underlying critical factors affecting failure may help in reducing the risk of abrupt failures and possibly prolong the 3DIM tool life. A hypothesis that the cooling time of the Injection Moulding (IM) process is a critical factor for 3DIM tool failure has been proposed. The failure hypothesis has been validated by theoretical calculations, FEA simulations and experimental investigations. Experiments were performed using two different materials for the 3DIM tool (Visijet M3-X and Digital ABS) and an engineering thermoplastic (Lexan 943-A) as the moulding material. Results showed that cooling time was a critical factor on tool life and managing the thermal loading on a 3DIM tool could lead to increased tool life. The paper identifies cooling time as the critical factor affecting 3DIM tool life and presents a cooling regime that could possibly lead to prolonged tool life.