Zeolite A was synthesized using the coal ash from Siderópolis/RS - Brazil. The synthesis was based on a standard IZA synthesis using coal ash as the Si and Al source. XRF analysis showed that the coal ash has a Si/Al ratio of 1.52, which is close to the Si/Al ratio required to produce zeolite A (1.0). The synthesized materials were analyzed by XRD, SEM and N2 adsorption. More crystalline materials were obtained during synthesis when an additional treatment was applied at a temperature of 353 K at the dissolution of NaOH step. The product formed after 4 hours was the most crystalline, but even the product formed after 1 hour proved to be better than that formed using the standard 4 hours IZA synthesis. The zeolites synthesized by this method had an adsorption capacity of 120 mg.g-1 for Ca2+, half the capacity of commercial zeolite A (300 mg.g-1). It was not possible to obtain blue or green pigments using the synthesized zeolite A

In this memory effect study, hydrotalcite-type compounds in the lamellar double hydroxide-like (LDH)/zeolite A composite material were analyzed using X-Ray Diffration XRD) in situ experiments. Three samples were analyzed: Al,Mg-LDH, Al,Mg-LDH/ZA composite, and a physical mixture (50/50 wt%) of zeolite A and Al,Mg-LDH. The Al,Mg-LDH sample was treated at 500 °C in an O₂ atmosphere and subsequently rehydrated. The Al,Mg-LDH/ZA composites had three treatments: one was performed at 300 °C in a He atmosphere, and two treatments were performed with an O₂ atmosphere at 300 and 500 °C. In the physical mixture, two treatments were carried out under O₂ flow at 500 °C and under He flow at 300 °C. Both went through the rehydration process. All samples were also analyzed by energy dispersive spectroscopy (EDS) and scanning electron microscopy (SEM). The results show that the LDH phase in the Al,Mg-LDH/ZA compounds has memory effects, and thus, the compound can be calcined and rehydrated. For the LDH in the composite, the best heat treatment system is a temperature of 300 °C in an inert atmosphere.

Here, we present the synthesis and structure determination of the new zeolite ITQ-62. Its structure was determined via ultra-fast electron diffraction tomography and refined using powder XRD data of the calcined material. This new zeolite contains a tridirectional channel system of highly distorted 8-rings, as well as a monodirectional 12-ring channel system.

Wastewater from the oil industry is a major problem for aqueous environments due to its complexity and estimated volume of approximately 250 million barrels per day. The combination of these petroleum pollutants creates risks to human health, and their removal from the environment is considered a major problem in the world today. Thus, this work has the objective of studying the treatment of this type of effluent through the adsorption method using the following exchange materials: cationic, anionic, their combination by a sequential method, and a composite material. Zeolite A, a layered double hydroxide (LDH), and the new composite material formed by zeolite A and LDH structures were synthesized for this study. All were used for the simultaneous treatment of cations and anions in a complex sample such as water produced from petroleum production. The composite demonstrated an excellent ability to simultaneously remove cations and anions. The results obtained after the different treatment modes of the effluent using different materials varied from 85% to 100% for the removal of cations and from 56% to 99.7% for the removal of anions.