Room-temperature ionic liquids (RTILs) are promising candidates for a broad range of “green” applications, for which their interaction with solid surfaces plays a crucial role. In this high-energy x-ray reflectivity study, the temperature-dependent structures of three ionic liquids with the tris(pentafluoroethyl)trifluorophosphate anion in contact with a charged sapphire substrate were investigated with submolecular resolution. All three RTILs show strong interfacial layering, starting with a cation layer at the substrate and decaying exponentially into the bulk liquid. The observed decay length and layering period point to an interfacial ordering mechanism, akin to the charge inversion effect, which is suggested to originate from strong correlations between the unscreened ions. The observed layering is expected to be a generic feature of RTILs at charged interfaces.

The differential capacitance of the electrical double layer at glassy carbon, platinum and gold electrodes immersed in various ionic liquids was measured using impedance spectroscopy. We discuss the influence of temperature, the composition of the ionic liquids and the electrode material on the differential capacitance/potential curves. For different systems these curves have various overall shapes, but all include several extremes and a common minimum near the open circuit potential. We attribute this minimum to the potential of zero charge (PZC). Significantly, the differential capacitance generally decreases if the applied potential is large and moving away from the PZC. This is attributed to lattice saturation [A. A. Kornyshev, J. Phys. Chem. B, 2007, 111, 5545] effects which result in a thicker double layer. The differential capacitance of the double layer grows and specific adsorption diminishes with increasing temperature. Specific adsorption of both cations and anions influences the shapes of curves close to the PZC. The general shape of differential capacitance/potential does not depend strongly on the identity of the electrode material.