Carbon-fiber-reinforced plastic (CFRP) is a popular material possessing great properties, such as strength, lightness, and resistance to corrosion and the environment. Important steps in the production of various parts made of CFRP are surface structuring, milling, drilling and cutting processes. Here, we propose to use ultrashort pulse lasers to achieve the high-quality, low-heat-affected-zone ablation of CFRP. We investigated the ablation efficiency dependence on the processing parameters, such as the pulse duration, pulse energy and pulse overlap. We showed that good-quality results could be achieved using just low-/mid-average-power femtosecond laser equipment. We also discuss further cutting process optimization possibilities using ultrashort pulse lasers and show the possibility of HAZ-free CFRP cutting by femtosecond laser ablation.

Carbon-fiber-reinforced plastic (CFRP) machining by ultrashort-pulse lasers promises high precision but is limited due to the heterogeneous epoxy–carbon fiber structure, which creates heat-affected zones and variable kerf quality. This work investigates synthesized copper hydroxyphosphate as a laser-absorbing additive to improve femtosecond (1030 nm) laser ablation of CFRP. Copper hydroxyphosphate particles were synthesized hydrothermally and incorporated into an epoxy matrix to produce single-ply CFRP laminates. Square patterns (0.5 × 0.5 mm) were ablated with a pulse energy of 0.5–16 μJ. Then, ablated volumes were profiled and materials characterized by SEM and EDS. In neat epoxy the copper additive reduced optimum ablation efficiency and decreased penetration depth, while producing smoother, less porous surfaces. In contrast, CFRP with copper hydroxyphosphate showed increased efficiency and higher penetration depth. SEM and EDS analyses indicate more uniform matrix removal and retention of resin residues on fibers. These results suggest that copper hydroxyphosphate acts as a local energy absorber that trades volumetric removal for improved surface quality in epoxy and enhances uniformity and process stability in CFRP femtosecond laser machining.

Carbon fiber reinforced plastics (CFRP) machining by ultrashort pulse lasers promises high precision but it is limited due to heterogeneous epoxy – carbon fiber structure, which creates heat-affected zones and variable kerf quality. This work investigates synthesized copper hydroxyphosphate as a laser-absorbing additive to improve femtosecond (1030 nm) laser ablation of CFRP. Copper hydroxyphosphate particles were synthesized hydrothermally and incorporated into an epoxy matrix to produce single-ply CFRP laminates. Square patterns (0.5×0.5 mm) were ablated with a pulse energy 0.5–16 μJ. Then ablated volumes were profiled and materials characterized by SEM and EDS. In neat epoxy the copper additive reduced optimum ablation efficiency and decreased penetration depth, while producing smoother, less porous surfaces. In contrast, CFRP with copper hydroxyphosphate showed increased efficiency and higher penetration depth. SEM and EDS analysis indicate more uniform matrix removal and retention of resin residues on fibers. These results suggest that copper hydroxyphosphate acts as a local energy absorber that trades volumetric removal for improved surface quality in epoxy and enhances uniformity and process stability in CFRP femtosecond laser machining.