Waterborne polyurethane coatings (WPU) are widely used in various types of coatings due to their environmental friendliness, rich gloss, and strong adhesion. However, their inferior mechanical properties and solvent resistance limit their application on the surface of wood products. In this study, graphene oxide (GO) with nanoscale size, large surface area, and abundant functional groups was incorporated into WPU by chemical grafting to improve the dispersion of GO in WPU, resulting in excellent mechanical properties and solvent resistance of WPU coatings. GO with abundant oxygen-containing functional groups and nanoscale size was prepared, and maintained good compatibility with WPU. When the GO concentration was 0.7 wt%, the tensile strength of GO-modified WPU coating film increased by 64.89%, and the abrasion resistance and pendulum hardness increased by 28.19% and 15.87%, respectively. In addition, GO also improved the solvent resistance of WPU coatings. The chemical grafting strategy employed in this study provides a feasible way to improve the dispersion of GO in WPU and provides a useful reference for the modification of waterborne wood coatings.

Under a global carbon-neutralizing environment, renewable wood is a viable alternative to non-renewable resources due to its abundance and high specific strength. However, fast-growing wood is hard to be applied extensively due to low mechanical strength and poor dimensional stability and durability. In this study, epoxy-acrylic resin-modified wood was prepared by forming a functional monomer system with three monomers [glycidyl methacrylate (GMA), maleic anhydride (MAN), and polyethylene glycol-200-dimethylacrylic acid (PEGDMA)] and filling into the wood cell cavity. The results showed that in the case of an optimal monomer system of nGMA:nPEGDMA = 20:1 and an optimal MAN dosage of 6%, the conversion rate of monomers reached 98.01%, the cell cavity was evenly filled by the polymer, with the cell wall chemically bonded. Thus, a bonding strength of as high as 1.13 MPa, a bending strength of 112.6 MPa and an impact toughness of 74.85 KJ/m² were applied to the modified wood, which presented excellent dimensional stability (720 h water absorption: 26%, and volume expansion ratio: 5.04%) and rot resistance (loss rates from white rot and brown rot: 3.05% and 0.67%). Additionally, polymer-modified wood also exhibited excellent wear resistance and heat stability. This study reports a novel approach for building new environmentally friendly wood with high strength and toughness and good structural stability and durability.

Wood is a viable alternative to traditional steel, cement, and concrete as a structural material for building applications, utilizing renewable resources and addressing the challenges of high energy consumption and environmental pollution in the construction industry. However, the vast supply of fast-growing poplar wood has bottlenecks in terms of low strength and dimensional stability, making it difficult to use as a structural material. An environmentally friendly acrylic resin system was designed and cured in this study to fill the poplar cell cavities, resulting in a new type of poplar laminated veneer lumber with improved mechanical strength and dimensional stability. The optimized acrylic resin system had a solid content of 25% and a curing agent content of 10% of the resin solid content. The cured filled poplar veneer gained 81.36% of its weight and had a density of 0.69 g/cm³. The static flexural strength and modulus of elasticity of the further prepared laminated veneer lumber were 123.12 MPa and 12,944.76 MPa, respectively, exceeding the highest flexural strength required for wood structural timber for construction (modulus of elasticity 12,500 MPa and static flexural strength 35 MPa). Its tensile strength, impact toughness, hardness, attrition value, water absorption, water absorption thickness expansion, and water absorption width expansion were 58.81%, 19.50%, 419.18%, 76.83%, 44.38%, 13.90%, and 37.60% higher than untreated laminated veneer lumber, demonstrating improved mechanical strength and dimensional stability, significantly. This method provides a novel approach to encouraging the use of low-value-added poplar wood in high-value-added structural building material applications.

Paper-based packaging materials have gained attention from academia and industry for their outstanding environmental sustainability advantages. However, they still encounter major challenges, such as low mechanical strength and inadequate functionality, hindering the replacement of unsustainable packaging materials. Inspired by the remarkable strength of trees provided by cellulose fibers and the water and heat protection of trees provided by bark, this study developed a new biomass-based packaging material (SNC-C) that combines strength, thermal insulation, and water resistance. The material was created by simply blending straw nanocellulose (SNC) with oak bark (i.e., cork), which naturally provides water-resistant, thermal insulation, and unique regenerative properties. The dense layered structure formed entirely by SNC generates a tensile strength reaching up to 60.93 MPa. With the cork cavity structure, the heat transfer rate of the obtained material is reduced to 2.90–3.01 °C/(cm·min). The combining of the closed-cell structure and the suberin component of the cork results in a low water vapor transmission rate (WVTR) of the material of 400.30 g/(m²·24 h). This all-biomass material with excellent performance and low environmental footprint offers a promising solution for the development of sustainable multifunctional packaging materials.