Variations in the microstructural morphology with building direction during selective laser melting (SLM) result in the anisotropic mechanical properties of the specimens, while heat treatment effectively reduces this anisotropy. The degree of anisotropy of the material can be assessed by calculating the variance (σ) of the mechanical properties (strength, hardness) at different building directions at different temperatures. In this work, the effects of heat treatment temperatures (450°, 750 °C, and 1050 °C) and building directions (0°, 45°, 60°, and 90°) on the microstructure, hardness, and tensile properties of selective laser melting (SLM) SS316L were investigated. Unheated SLM SS316L specimens exhibit significant anisotropy (σ_UTS = 16.67, σ_UE = 9.60, and σ_HV = 9.60), while heat treatment effectively reduces this anisotropy. As the heat treatment temperature increases, the melt pool boundaries disappear and grains become uniform at 750 °C, significantly reducing the anisotropy of the mechanical properties (σ_UTS = 14.65, σ_UE = 4.33, σ_HV = 6.72). At 1050 °C, the grain size increases slightly, resulting in a minor rise in anisotropy (σ_UTS = 14.93, σ_UE = 4.97, σ_HV = 8.39) compared to that seen at 750 °C. After heat treatment, the SLM SS316L specimen heated at 450 °C shows the lowest anisotropy. Notably, the specimens built in the 0° direction and heated at 450 °C exhibit finer sub-grains and enhanced mechanical properties, achieving a hardness of 244.43 HV, a tensile strength of 655.85 MPa, and an elongation of 21.25%.

At the initial rolling temperature of 400 °C, ZK60 magnesium alloy was hot rolled by three different rolling paths with different roll speed ratios (RSR) of 1:1.15, 1:1.2, and 1:1.5, respectively. The effects of different rolling processes on the microstructure and mechanical properties of the alloy were studied. The microstructure, plasticity, strength, hardness, and texture intensity of rolled samples were analyzed in this work. The results show that the microstructure uniformity of the alloy under multi-path asynchronous rolling (MAR) is significantly improved, which improves the mechanical properties of the material to a certain extent, and effectively weakens the texture intensity of the basal plane and reduces the anisotropy. The amount of randomly oriented grains of ZK60 magnesium alloy rolled by the C-1.5 (path C combined with the RSR of 1:1.5) process are significantly increased, which significantly weakens the basal texture and improves the ductility of the alloy, greatly enhancing the processing and formability of ZK60 magnesium alloy.