Laser induced damage of fused silica optics occurs primarily on optical surface or subsurface resulting from various defects produced during polishing/grinding process. Many new kinds of surface treatment processes are explored to remove or control the defects on fused silica surface. In this study, we report a new application of reaction ion etching (RIE)-based surface treatment process for manufacture of high quality fused silica optics. The influence of RIE processes on laser damage resistance as a function of etching depth and the evolution of typical defects which are associated with laser damage performance were investigated. The results show that the impurity element defects and subsurface damage on the samples surface were efficiently removed and prevented. Pure silica surface with relatively single-stable stoichiometry and low carbon atomic concentration was created during the etching. The laser damage resistance of the etched samples increased dramatically. The increase of roughness and ODC point defect with deeper etching are believed to be the main factors to limit further increase of the damage resistance of fused silica. The study is expected to contribute to the development of fused silica optics with high resistance to laser induced degradation in the future.

Hexagonally ordered arrays of polystyrene (PS) microspheres were prepared by a modified air-water self-assembly method. A detailed analysis of the air-water interface self-assembly process was conducted. Several parameters affect the quality of the monolayer colloidal crystals, i.e., the colloidal microsphere concentration on the latex, the surfactant concentration, the polystyrene microsphere diameter, the microsphere polydispersity, and the degree of sphericity of polystyrene microspheres. An abrupt change in surface tension was used to improve the quality of the monolayer colloidal crystal. Three typical microstructures, i.e., a cone, a pillar, and a binary structure were prepared by reactive-ion etching using a high-quality colloidal crystal mask. This study provides insight into the production of microsphere templates with flexible structures for large-area patterned materials.

The reactive ion etching (RIE) process of fused silica is often accompanied by surface contamination, which seriously degrades the ultraviolet laser damage performance of the optics. In this study, we find that the contamination behavior on the fused silica surface is very sensitive to the RIE process which can be significantly optimized by changing the plasma generating conditions such as discharge mode, etchant gas and electrode material. Additionally, an optimized RIE process is proposed to thoroughly remove polishing-introduced contamination and efficiently prevent the introduction of other contamination during the etching process. The research demonstrates the feasibility of improving the damage performance of fused silica optics by using the RIE technique.