Background: This research paper aims to investigate the effectiveness of gender identification utilizing palatal rugae Materials and Methods: The size of the sample that was selected included 100 people. They were made up of 50 men and 50 women, all in between the ages of 18 and 25. To examine their palatal rugae patterns, casts were made after taking maxillary impressions. Based on the size and rugae amount found on the left as well as the right sides, the palatal rugae patterns were investigated. Rugae patterns have been recognized based on the categorization provided by Thomas and Kotze (1983). Statistical Analysis: Chi-square analysis has been used. Results: There were comparative variations in the shape of rugae patterns among male and female individuals. The study revealed that the circular pattern was higher in males (P < 0.01) as compared to females and the unification pattern was comparatively greater in females (P < 0.05) as compared to males. The most predominant pattern that was seen in both genders was the wavy pattern that was seen to be present in 57.17% of males and 53.42% of females. The rugae number on the right and left sides did not exhibit any significant variations. Conclusions: This research thus exhibits a relevant difference in patterns of rugae and also confirms the uniqueness of patterns in each individual. Hence, it could be utilized as an adjunct to other tools for identification in the forensic sciences.

Aim: The aim of the study is to investigate the effect of joint surface preparations and chemical surface treatment given to prepared surface on the transverse strength of repaired denture base resin. Methodology: Two hundred and twenty specimens (DPI India) were randomly allocated into eight groups (n = 10), according to the combination of joint surface preparation (Butt joint, 45° bevel, and rounded joint) and chemical surface treatment (methylene chloride, ethyl acetate, and methyl methacrylate) for 30 and 60 s each. Specimens, after surface treatment, were repaired with self-cured resin (DPI India) and then subjected to 3-point bending test to measure transverse strength. Fractured surfaces were viewed under stereomicroscope and subjected to AutoCAD analysis to determine type of failure (adhesive or cohesive) and measure their area. Measurement data were analyzed by one-way analysis of variance, paired t-test, Dunnett's D test, and multiple comparison Bonferroni t-test, with a 5% significance level. Results: Most of the comparisons between the test specimens were statistically significant. Specimens (methylene chloride for 60 s and rounded joint) show 60%–70% gain of strength. Conclusions: For providing better bond strength to a repaired specimen, the segment of fractured specimens to be provided “Rounded joint” preparation with etching by methylene chloride for 60 s.

The changes in interproximal contact between implant supported prosthesis (ISP) and adjacent natural tooth is of interest to dentists. Hence, we evaluated the tightness of proximal contact (PCT) between adjacent natural tooth and ISP by applying a digital force gauge spanning over a period of 1.5 year with a regular follow-up of 3, 6, and 12 months.80 patients who received ISP were included in this study. In order to measure the PCT, every patient seated in the identical upright position in the dentist chair. The digital force gauge was used to take measurements for mesial PCT and distal PCT. The mesial as well as distal interproximal contacts was more tight as in case of natural tooth adjacent to other natural tooth as compared to interproximal contacts between ISP and adjacent natural tooth. It was also observed that as the time progressed there was decrease in PCT values in both categories. After 12 month follow up 30.6% cases in category 2 while 21.2% cases in category 1 showed complete loss of interproximal contact. There is significant change in proximal contact tightness in interproximal area between implant supported prosthesis and adjacent natural tooth over a period of time and necessary measures should be taken to prevent or reduce it.

Background: This research study aimed to evaluate and compare the capability of four various bite registration materials to reproduce precise interocclusal relationships in the vertical dimension Materials and Methods: Ideal maxillary and mandibular casts were mounted on the semi-adjustable articulator in maximum intercuspation after mock tooth preparation on 46, 47, and 48. Models were scanned by the Medit T500 Dental Lab Scanner, and initial reading was noted at the predetermined points. Ten interocclusal bite registrations were made using four materials (CADbite, Jet Bite, Ramitec, and Aluwax). The mandibular model was demounted and again remounted using the interocclusal records, and the final reading was noted after scanning. Results: Ramitec showed superior results when compared to polyvinyl bite registration material and Aluwax, but the differences between Ramitec, CADbite, and Jet Bite were nonsignificant. Conclusions: Although all four materials are suitable for clinical use, elastomeric materials showed superior results. In that, polyether was found to be the best.

Purpose: Acrylic denture base tends to fracture frequently during their service due to poor strength. The surface roughness of denture base is a critical property because denture base with rough surface will cause accumulation of food particles, thereby leading plaque retention. Microbes such as candida albicans are seen inhabitating the surface. Materials and Methods: Conventional heat cure denture base reins(DPI) and heat cure denture base resin with incorporation of 15wt% aluminium oxide was studied in two groups with 20 samples each. A mold of size 65 mm × 10 mm × 3 mm (ISO Standard) was obtained by investing brass rectangles. About forty specimens were prepared. Specimens were divided into two groups (n = 20) coded A and B. Group A was the control group (n = 20) without addition of aluminum oxide. Group B was the experimental group (n = 20) with addition of 15 wt % aluminum oxide. All the specimens were stored in distilled water for 14 days. The flexural strength was measured using a three-point bending test in a universal testing machine, and the surface roughness was measured using contact-type profilometer. Results: Incorporation of 15wt% aluminum oxide leads to a significant increase in flexural strength and surface roughness of conventional heat-cure denture base resin.

Digitalization in dentistry, encompassing use of digital technology, is indeed the dominant force, impacting every aspect of the profession. Therefore, it is of interest to evaluate and comprehend dental technicians’ knowledge, attitude and practice related to digital laboratory procedures in India. A questionnaire-based cross-sectional research was performed among registered dental technicians across India and descriptive statistics were utilized to calculate frequency distributions and chi-square for relationships among variables. The mean knowledge score (4.63±2.18), attitude score (4.52±2.19) and the practice score (4.55±2.14) was substantially exceeded in the dental technicians working in the south zone compared to other zones. The dental technicians employed at private dental laboratory had greater knowledge score (4.04±1.75), attitude score (3.96±1.74) and practice score (3.98±1.72) compared to those working in dental college. The dental technicians of south zone exhibited greater attitude, knowledge and practice of digital dental laboratory procedures than other zones across India.