Titania nanotube (TNT) coatings were produced using low-potential anodic oxidation of Ti6Al4V substrates in the potential range 3–20 V. They were analysed by X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). The wettability was estimated by measuring the contact angle when applying water droplets. The bioactivity of the TNT coatings was established on the basis of the biointegration assay (L929 murine fibroblasts adhesion and proliferation) and antibacterial tests against Staphylococcus aureus (ATCC 29213). The photocatalytic efficiency of the TNT films was studied by the degradation of methylene blue under UV irradiation. Among the studied coatings, the TiO₂ nanotubes obtained with the use of 5 V potential (TNT5) were found to be the most appropriate for medical applications. The TNT5 sample possessed antibiofilm properties without enriching it by additional antimicrobial agent. Furthermore, it was characterized by optimal biocompatibility, performing better than pure Ti6Al4V alloy. Moreover, the same sample was the most photocatalytically active and exhibited the potential for the sterilization of implants with the use of UV light and for other environmental applications.

Bioactivity investigations of titania nanotube (TNT) coatings enriched with silver nanograins (TNT/Ag) have been carried out. TNT/Ag nanocomposite materials were produced by combining the electrochemical anodization and chemical vapor deposition methods. Fabricated coatings were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and Raman spectroscopy. The release effect of silver ions from TNT/Ag composites immersed in bodily fluids, has been studied using inductively coupled plasma mass spectrometry (ICP-MS). The metabolic activity assay (MTT) was applied to determine the L929 murine fibroblasts adhesion and proliferation on the surface of TNT/Ag coatings. Moreover, the results of immunoassays (using peripheral blood mononuclear cells—PBMCs isolated from rats) allowed the estimation of the immunological activity of TNT/Ag surface materials. Antibacterial activity of TNT/Ag coatings with different morphological and structural features was estimated against two Staphylococcus aureus strains (ATCC 29213 and H9). The TNT/Ag nanocomposite layers produced revealed a good biocompatibility promoting the fibroblast adhesion and proliferation. A desirable anti-biofilm activity against the S. aureus reference strain was mainly noticed for these TiO₂ nanotube coatings, which contain dispersed Ag nanograins deposited on their surface.

The 5-aminolevulinic acid (5-ALA) prodrug is widely used in clinical applications, primarily for skin cancer treatments and to visualize brain tumors in neurosurgery. Unfortunately, its applications are limited by unfavorable pharmacological properties, especially low lipophilicity; therefore, efficient nanovehicles are needed. For this purpose, we synthesized and characterized two novel water-soluble fullerene nanomaterials containing 5-ALA and D-glucuronic acid components. Their physicochemical properties were investigated using NMR, XPS, ESI mass spectrometry, as well as TEM and SEM techniques. In addition, HPLC and fluorescence measurements were performed to evaluate the biological activity of the fullerene nanomaterials in 5-ALA delivery and photodynamic therapy (PDT); additional detection of selected mRNA targets was carried out using the qRT-PCR methodology. The cellular response to the [60]fullerene conjugates resulted in increased levels of ABCG2 and PEPT-1 genes, as determined by qRT-PCR analysis. Therefore, we designed a combination PDT approach based on two fullerene materials, C₆₀-ALA and C₆₀-ALA-GA, along with the ABCG2 inhibitor Ko143.

Siderite (FeCO₃) is an iron-bearing carbonate mineral that is the most abundant sedimentary iron formation on Earth. Mineralogical alteration of four siderite samples annealed at temperatures 200 °C, 300 °C, 400 °C, 500 °C, 750 °C, and 1000 °C in an O₂ and a CO₂ atmosphere were investigated using such tools as X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), the X-ray fluorescence (XRF) method, differential scanning calorimetry and thermogravimetric analysis (DSC/TGA), and Mössbauer spectroscopy measurements. The decomposition of three siderite samples with similar iron content in the oxygen atmosphere took place in the temperature range of 340–607 °C. This process begins at approximately ~100 °C higher under a reducing atmosphere, but it is completed just above 600 °C, which is a temperature comparable to decomposition in an oxidizing atmosphere. These processes are shifted toward higher temperatures for the fourth sample with the lowest iron but the highest magnesium content. Magnetite, hematite, and maghemite are products of siderite decomposition after annealing in the oxygen atmosphere in the temperature range 300–500 °C, whereas hematite is the main component of the sample detected after annealing at 750 °C and 1000 °C. Magnetite is the main product of siderite decomposition under the CO₂ atmosphere. However, hematite, maghemite, wüstite, and olivine were also present in the samples after annealing above 500 °C in this atmosphere.