Additive manufacturing (AM) is the fabrication of real three-dimensional objects from metals, ceramics, or plastics by adding material, usually as layers. There are several variants of AM; among them material extrusion (ME) is one of the most versatile and widely used. In MEAM, molten or viscous materials are pushed through an orifice and are selectively deposited as strands to form stacked layers and subsequently a three-dimensional object. The commonly used materials for MEAM are thermoplastic polymers and particulate composites; however, recently innovative formulations of highly-filled polymers (HP) with metals or ceramics have also been made available. MEAM with HP is an indirect process, which uses sacrificial polymeric binders to shape metallic and ceramic components. After removing the binder, the powder particles are fused together in a conventional sintering step. In this review the different types of MEAM techniques and relevant industrial approaches for the fabrication of metallic and ceramic components are described. The composition of certain HP binder systems and powders are presented; the methods of compounding and filament making HP are explained; the stages of shaping, debinding, and sintering are discussed; and finally a comparison of the parts produced via MEAM-HP with those produced via other manufacturing techniques is presented.

Within this paper, we are dealing with a mixture of thermoplastic polymer that is filled with inorganic fillers at high concentrations up to 60 vol.%. A high number of particles in the compound can substantially change the rheological behaviour of the composite and can lead to problems during processing in the molten state. The rheological behaviour of highly filled materials is complex and influenced by many interrelated factors. In the present investigation, we considered four different spherical materials: steel, aluminium alloy, titanium alloy and glass. Particles with similar particle size distribution were mixed with a binder system at different filling grades (30–60 vol.%). We showed that the rheological behaviour of highly filled materials is significantly dependent on the chemical interactions between the filler and matrix material. Moreover, it was shown that the changes of the particle shape and size during processing lead to unexpected rheological behaviour of composite materials as it was observed in the composites filled with glass beads that broke at high contents during processing.