This study focuses on the influence of local moringa oil on the performances of lubricants obtained from a blend of dodecane and pristine or fluorinated carbon nanofibers at ambient temperature. The friction experiments have been evaluated using a reciprocating ball on a plane tribometer. Moringa oil is used as a bio-additive in lubricant formulations. First, the addition of a small amount of moringa oil to dodecane allowed a reduction of about 50% of the base oil friction performances. Second, a comparative study on the friction properties of their blends with pristine carbon nanofibers (CNFs) and fluorinated ones (CF_0.85) was investigated, based on which they were intended to be used as solid lubricant additives. An adsorption effect of fatty acid molecules is observed in CNFs particles unlike CF_0.85. Whatever was the percentage of moringa oil added, more promising results were obtained with CF_0.85. Physicochemical characterizations of the tribofilms evidence the good antiwear properties of the lubricants.

Vegetable oils in the lubricant field are largely studied. Their efficiency depends on their viscosity parameters and their fatty acid composition. The actions of moringa oil used as a lubricant base and as a lubricant additive have been shown in this work. Graphite, carbon nanofibers, and carbon nanodots are carbon phases of different shapes used as solid additives. The tribological performances of lubricant blends composed of between 0.5 and 1 wt.% of particles have been evaluated using a ball-on-plane tribometer under an ambient atmosphere. No additional surfactant was used. The positive and important actions of a small amount of moringa oil added in the lubricant formulas are demonstrated. The results obtained allow us to point out the influence of the type and shape of particles. Physicochemical investigations allow us to propose a synergistic effect between the particles and moringa oil as additives in dodecane.