Continuous fibers with outstanding mechanical performance due to the continuous enhancement effect, show wide application in aerospace, automobile, and construction. There has been great success in developing continuous synthetic fiber-reinforced composites, such as carbon fibers or glass fibers; however, most of which are nonrenewable, have a high processing cost, and energy consumption. Bio-sourced materials with high reinforced effects are attractive alternatives to achieve a low-carbon footprint. In this study, continuous bamboo fiber-reinforced polyethylene (CBF/PE) composites were prepared via a facile two-step method featuring alkali treatment followed by 3D printing. Alkali treatment as a key processing step increases surface area and surface wetting, which promote the formation of mechanical riveting among bamboo fibers and matrix. The obtained treated CBF (T-CBF) also shows improved mechanical properties, which enables a superior reinforcement effect. 3D printing, as a fast and local heating method, could melt the outer layer PE tube and impregnate molten plastics into fibers under pressure and heating. The resulting T-CBF/PE composite fibers can achieve a tensile strength of up to 15.6 MPa, while the matrix PE itself has a tensile strength of around 7.7 MPa. Additionally, the fracture morphology of printed bulks from composite fibers shows the alkali-treated fibers–PE interface is denser and could transfer more load. The printed bulks using T-CBF/PE shows increased tensile strength and Young’s modulus, with 77%- and 1.76-times improvement compared to pure PE. Finally, the effect of printing paraments on mechanical properties were analyzed. Therefore, this research presents a potential avenue for fabricating continuous natural fiber-reinforced composites.

Zirconia ceramics are promising materials for restoration and are widely used in the field of artificial teeth. However, wear resistance affects the longevity of artificial teeth. In this study, peacock tail feather micro-textures and groove micro-textures are prepared on the surfaces of zirconia ceramics via the laser ablation technique to improve their tribological properties. The effects of micro-textures on the surface wettability and tribological properties of zirconia ceramics are studied. The micro-textures improve the surface wettability and tribological properties of zirconia ceramics. The average coefficient of friction of peacock tail feather micro-textured samples decreases by 53% compared to that of the samples without micro-textures. Different operating conditions affect the friction properties of zirconia ceramics. The samples have the best friction performance when the rotational speed, load, and acid/alkaline environment are 200 r/min, 15 N, and weakly alkaline, respectively. Furthermore, the mechanism by which surface micro-textures reduce frictional wear is as follows: the textured grooves store debris, and the bottom edge of the textured groove acts as a cutting tool to cut debris, preventing debris from scratching the surface. The micro-textures store lubricant and form a liquid film on the ceramic surface to reduce wear.

ZrO₂ ceramics, known for their high strength and wear resistance, are ideal for artificial joints. This study enhanced the friction performance of these joints by fabricating textured structures (50 μm width and 20–25 μm depth) on the ceramic surface. Friction tests, conducted at 200 r/min for 30 min with a 5–20 N load and lubricant concentration of 15–60 mg/mL using PEEK balls, showed that textured joints outperformed untextured ones. The symmetrical triangular structure had the lowest coefficient of friction and the best hydrophilicity, with a 53.0% reduction in the coefficient of friction and a 57.4% reduction in the contact angle compared to the untextured structure. The textures effectively store the PEEK residue and facilitate the smooth movement of the worn ball. Concurrently, the textured structure stores some of the lubricant, which reduces the static pressure during fluid flow by 12.6%. Overall, the friction performance of ZrO₂ ceramic artificial joints was significantly improved by the textured structures.