Refractory high-entropy alloys (RHEAs) are promising materials used at high temperature, but their low plasticity restricts their application. Based on the valence electron concentration (VEC) principle, four kinds of RHEAs (ZrTiHfV_0.5Nb_0.5, Zr_2.0TiHfVNb_2.0, ZrTiHfNb_0.5Mo_0.5, and ZrTiHfNb_0.5Ta_0.5) are designed (VEC < 4.5). The experimental results show that the plasticity of these alloys was greatly improved: the static compressive strain was higher than 50% at room temperature (RT), and some elongations were produced in the tensile process. Moreover, the microstructure and phase composition are discussed in detail. The addition of Nb, Mo, and Ta contributed to the high-temperature strength. Finally, the dynamic mechanical properties of these RHEAs with coordination between strength and plasticity are investigated.

Energetic composite materials (ECMs) are the basic materials of polymer binder explosives and composite solid propellants, which are mainly composed of explosive crystals and binders. During the manufacturing, storage and use of ECMs, the bonding surface is prone to micro/fine cracks or defects caused by external stimuli such as temperature, humidity and impact, affecting the safety and service of ECMs. Therefore, substantial efforts have been devoted to designing suitable self-healing binders aimed at repairing cracks/defects. This review describes the research progress on self-healing binders for ECMs. The structural designs of these strategies to manipulate macro-molecular and/or supramolecular polymers are discussed in detail, and then the implementation of these strategies on ECMs is discussed. However, the reasonable configuration of robust microstructures and effective dynamic exchange are still challenges. Therefore, the prospects for the development of self-healing binders for ECMs are proposed. These critical insights are emphasized to guide the research on developing novel self-healing binders for ECMs in the future.