The purpose of this study was to compare: a new five-layered poly (L–lactide–co–caprolactone) (PLC) membrane and small intestinal submucosa (SIS) as a control in rat urinary bladder wall regeneration. The five-layered poly (L–lactide–co–caprolactone) membrane was prepared by an electrospinning process. Adipose tissue was harvested from five 8-week old male Wistar rats. Adipose derived stem cells (ADSCs) were seeded in a density of 3×10⁶ cells/cm² onto PLC membrane and SIS scaffolds, and cultured for 5-7 days in the stem cell culture medium. Twenty male Wistar rats were randomly divided into five equal groups. Augmentation cystoplasty was performed in a previously created dome defect. Groups: (I) PLC+ 3×10⁶ADSCs; (II) SIS+ 3×10⁶ADSCs; (III) PLC; (IV) SIS; (V) control. Cystography was performed after three months. The reconstructed urinary bladders were evaluated in H&E and Masson's trichrome staining. Regeneration of all components of the normal urinary bladder wall was observed in bladders augmented with cell-seeded SIS matrices. The urinary bladders augmented with SIS matrices without cells showed fibrosis and graft contraction. Bladder augmentation with the PLC membrane led to numerous undesirable events including: bladder wall perforation, fistula or diverticula formation, and incorporation of the reconstructed wall into the bladder lumen. The new five-layered poly (L–lactide–co–caprolactone) membrane possesses poorer potential for regenerating the urinary bladder wall compared with SIS scaffold.

Albumin is rarely used for electrospinning because it does not form fibres in its native globular form. This paper presents a novel method for electrospinning human albumin from a solution containing pharmaceutical grade protein and 25% polyethylene oxide (PEO) used as the fibre-forming agent. After spontaneous cross-linking at body temperature, with no further chemicals added, the fibres become insoluble and the excess PEO can be washed out. Albumin deposited along the fibres retains its native characteristics, such as its non-adhesiveness to cells and its susceptibility for degradation by macrophages. To demonstrate this we evaluated the mechanical properties, biocompatibility and biodegradability of this novel product. After subcutaneous implantation in mice, albumin mats were completely resorbable within six days and elicited only a limited local inflammatory response. In vitro, the mats suppressed cell attachment and migration. As this product is inexpensive, produced from human pharmaceutical grade albumin without chemical modifications, retains its native protein properties and fulfils the specific requirements for anti-adhesive dressings, its clinical use can be expedited. We believe that it could specifically be used when treating paediatric patients with epidermolysis bullosa, in whom non-healing wounds occur after minor hand injuries which lead to rapid adhesions and devastating contractures.

Electrospun nanofibers have widespread putative applications in the field of regenerative medicine and tissue engineering. When compared to naturally occurring collagen matrices, electrospun nanofiber scaffolds have two distinct advantages: they do not induce a foreign body reaction and they are not at risk for biological contamination. However, the exact substrate, structure, and production methods have yet to be defined. In the current study, tubular-shaped poly(L-lactide-co-caprolactone) (PLCL) constructs produced using electrospinning technology were evaluated for their potential application in the field of tissue regeneration in two separate anatomic locations: the skin and the abdomen. The constructs were designed to have an internal diameter of 3 mm and thickness of 200 μm. Using a rodent model, 20 PLCL tubular constructs were surgically implanted in the abdominal cavity and subcutaneously. The constructs were then evaluated histologically using electron microscopy at 6 weeks post-implantation. Histological evaluation and analysis using scanning electron microscopy showed that pure scaffolds by themselves were able to induce angiogenesis after implantation in the rat model. Vascularization was observed in both tested groups; however, better results were obtained after intraperitoneal implantation. Formation of more and larger vessels that migrated inside the scaffold was observed after implantation into the peritoneum. In this group no evidence of inflammation and better integration of scaffold with host tissue were noticed. Subcutaneous implantation resulted in more fibrotic reaction, and differences in cell morphology were also observed between the two tested groups. This study provides a standardized evaluation of a PLCL conduit structure in two different anatomic locations, demonstrating the excellent ability of the structure to achieve vascularization. Functional, histological, and mechanical data clearly indicate prospective clinical utilization of PLCL in critical size defect regeneration.