The present investigation introduces a novel approach, using As-Zn-Fe mining tailings (MT) and recycled bottle glass (cullet) to enable the manufacturing of a new glass for ornamental articles, with characteristics similar to those of soda–lime–silicate glass (SLS), and at the same time, immobilizing potentially toxic elements (PTEs) from mining tailings, which cause environmental pollution with severe risks to human health. The glass used was obtained from transparent glass bottles collected from urban waste, which were later washed to remove impurities and then crushed until they reached No. 70 mesh (212 μm) level; in the case of mining tailings, the sample used comes from the ore benefit process, with 96.8% of particles below the No. 50 mesh level (300 μm). Six mixtures were made by varying the composition of the mining tailings and glass, K₂CO₃ and H₃BO₃ as fluxes were also used in constant proportion. The mixtures were melted at 1370 °C, and later, the glass samples were cast on a steel plate at room temperature. The characteristics of the glasses were studied using thermal analysis (TA), X-ray diffraction (XRD), Fourier transform infrared (FTIR), and scanning electron microscopy (SEM). Likewise, their chemical resistance in acid and basic media and density were evaluated. The results unequivocally demonstrate the feasibility of manufacturing glasses with a light green color, the increase in the content of mining tailings increased the apparent T_g from 625 to 831 °C. Glasses with 17 and 21.3% MT presented lower density values due to a better-polymerized glass structure, attributed to the increase in SiO₂ and Al₂O₃ and the decrease in alkaline oxides, which allowed for the retention of PTEs in their structure.

The pursuit of thermal comfort in buildings is one of the main sources of energy consumption worldwide. To mitigate this expenditure, thermal insulation is required in construction. However, most conventional insulation materials come from non-renewable resources. Recently, different alternatives for generating more environmentally friendly insulation from biomass have been studied. However, when using biomass, care must be taken to avoid negatively impacting the food industry. One way to address this is to use biomass waste from previous manufacturing processes. The use of waste from the production of biofuel derived from castor beans (Ricinus communis) for the manufacture of thermal insulation was successfully implemented. Castor beans were collected and used to obtain biofuel. The waste was mixed with construction materials (lime, marble dust, and cement) in different concentrations. A device for measuring thermal conductivity was built and validated. The results of scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) are presented to characterize the material. A decrease in thermal conductivity was found in the construction material depending on the presence of micelle remnants left after oil extraction.