Detonation-produced hydroxyapatite coatings were studied by scanning electron microscopy (SEM), X-ray powder diffraction (XRD), Raman spectroscopy, and electron paramagnetic resonance (EPR) spectroscopy. The source material for detonation spraying was a B-type carbonated hydroxyapatite powder. The coatings consisted of tetracalcium phosphate and apatite. The ratio depended slightly on the degree of crystallinity of the initial powder and processing parameters of the coating preparation. The tetracalcium phosphate phase was homogeneous; the apatite phase contained defects localized on the sixfold axis and consisted of hydroxyapatite and oxyapatite. Technological factors contributing to the transformation of hydroxyapatite powder structure during coating formation by detonation spraying are discussed.

In this study, we report a significant enhancement in the performance of GaNAs-based single nanowire lasers through optimization of growth conditions, leading to a lower lasing threshold and higher operation temperatures. Our analysis reveals that these improvements in the laser performance can be attributed to a decrease in the density of localized states within the material. Furthermore, we demonstrate that owing to their excellent nonlinear optical properties, these nanowires support self-frequency conversion of the stimulated emission through second harmonic generation (SHG) and sum-frequency generation (SFG), providing coherent light emission in the cyan-green range. Mode-specific differences in the self-conversion efficiency are revealed and explained by differences in the light extraction efficiency of the converted light caused by the electric field distribution of the fundamental modes. Our work, therefore, facilitates the design and development of multiwavelength coherent light generation and higher-temperature operation of GaNAs nanowire lasers, which will be useful in the fields of optical communications, sensing, and nanophotonics.

The EPR studies of synthetic hydroxyapatite containing carbonate and nitrate ions exposed to γ-ray and UV irradiations have been performed. It has been found that γ irradiation leads to the formation of both NO ₃ ²⁻ and CO ₂ ⁻ paramagnetic centers, while the UV irradiation induces only NO ₃ ²⁻ centers. To explain this fact, the hypothesis has been proposed, according to which in the hydroxyapatites studied, there coexist complexes consisting of nitrate ions and shallow electron traps that serve as sources of secondary electrons during UV irradiation. The EPR spectroscopy parameters (g and A) of the detected centers have been determined and compared with similar centers in hydroxyapatite with a different impurity composition. The study of the thermal stability of the centers has demonstrated that, in the temperature range 20–300°C, the NO ₃ ²⁻ centers formed by UV irradiation are more stable than the same centers created by γ-ray irradiation.

The influence of calcination temperature on copper spatial localization in Y-stabilized ZrO2 powders was studied by attenuated total reflection, diffuse reflectance, electron paramagnetic resonance, transmission electron microscopy, electron energy loss, and energy-dispersive X-ray spectroscopies. It was found that calcination temperature rise in the range of 500–700 °C caused the increase of copper concentration in the volume of ZrO2 nanocrystals. This increase was due to Cu in-diffusion from surface complexes that contained copper ions linked with either water molecules or OH groups. This copper in-diffusion led also to an enhancement of absorption band peaked at ~270 nm that was ascribed to the formation of additional oxygen vacancies in nanocrystal volume. Further increasing of calcination temperature from 800 up to 1000 °C resulted in outward Cu diffusion accompanied by a decrease of the intensity of the 270-nm absorption band (i.e., oxygen vacancies’ number), the transformation of ZrO2 tetragonal (cubic) phase to monoclinic one as well as the enhancement of absorption band of dispersed and crystalline CuO in the 600–900 nm range.