Silver nanoparticles (Ag-NPs) adhered/inserted on textile fibers have an effective antimicrobial role. However, their release due to low adherence and their fate in the natural settings have been questioned in terms of toxicity level. In order to overcome this recurrent problem of adherence, the in situ formation of Ag-NPs in five textile fibers (cotton (untreated and chemically bleached), sheep’s wool, polyamide, and polyester) was assessed. Herein, the fibers were first immersed in a silver ion solution (1 g/L of AgNO₃) for ion saturation at room T for 24 h followed by draining fibers and their reimmersion this time in a strong chemical reducing solution (0.25 g/L of NaBH₄) at room T for 24 h. This latter step leads to the in situ formation of Ag-NPs where size (5 nm < size < 50 nm), surface covering concentration, and aggregation degree depend on the textile fiber kind as deduced from FESEM images. This simple lab chemical method allows instantaneous in situ formation of Ag-NPs onto fibers without the requirement of additional thermal treatment. Moreover, for natural fibers, the formation of Ag-NPs inside of them is also expected as confirmed from FESEM images in cotton cross sections. In complement, all textile fibers containing Ag-NPs (sheep’s wool 10 mg/g > untreated cotton 2.3 mg/g > bleached cotton 1 mg/g > polyamide 0.62 mg/g > polyester 0.28 mg/g) were submitted to interact with strong oxidants in an aqueous media (7.5% v/v of H₂O₂, 0.5 and 0.05 M of HNO₃ and ultrapure water as the control) using flow-through reactor experiments. Here, breakthrough curves reveal that the oxidative dissolution rate (given in mol/g min) of adhered Ag-NPs (ionic release) depends strongly on fiber nature, and nature and concentration of oxidant solution. In summary, this fundamental study suggests that Ag-NPs may be successfully adhered/inserted in natural fibers (wool and cotton) in a safety-design perspective with performant biocide properties as confirmed by using Bacillus subtilis.

In order to better understand the microtextural changes associated with serpentinization reactions, natural millimeter-sized olivine grains were experimentally reacted with alkaline NaOH and NaHCO₃ solutions at a temperature of 200 °C and for durations of 3 to 12 months. During hydration experiments, dissolution and precipitation were intimately correlated in time and space, with reaction products growing in situ, either as layered veins or as nearly continuous surface cover. In contrast, carbonation experiments showed a strong decoupling between both processes leading to essentially delocalized precipitation of the reaction products away from dissolution sites. Textural analyses of the samples using scanning electron microscopy, Raman spectroscopy, and X-ray synchrotron microtomography provided experimental evidence for a cause-and-effect relationship between in situ precipitation and intracrystalline reaction-induced cracking in olivine. Juvenile cracks typically nucleated at the tip of dissolution notches or on diamond-shaped pores filled with reaction products, and propagated through the olivine crystal lattice during the course of the reaction. The occurrence of new cracks at the tip of diamond-shaped pores, but also of tiny subspherical pores lining up along microcracks, indicated that fracturation and porosity networks were mutually driven, making serpentinization an extremely efficient alteration process over time. Alternatively, our data suggested that some form of porosity also developed in absence of fracturation, thus further highlighting the remarkable efficiency and versatility of serpentinization processes.