The exfoliation of graphene from pristine graphite in a liquid phase was achieved successfully via sonication followed by centrifugation method. Ultraviolet–visible (UV–vis) spectra of the obtained graphene dispersions at different exfoliation time indicated that the concentration of graphene dispersion increased markedly with increasing exfoliation time. The sheet-like morphology of the exfoliated graphene was revealed by Scanning Electron Microscopy (SEM) image. Further, the morphological change in different exfoliation time was investigated by Atomic Force Microscopy (AFM). A complete structural and defect characterization was probed using micro-Raman spectroscopic technique. The shape and position of the 2D band of Raman spectra revealed the formation of bilayer to few layer graphene. Also, Raman mapping confirmed the presence of uniformly distributed bilayer graphene sheets on the substrate.

Zinc oxide/Graphene (GZ) composites with different concentrations of ZnO were successfully synthesized through simple chemical precipitation method. The X-ray diffraction pattern and the micro-Raman spectroscopic technique revealed the formation of GZ composite, and the energy dispersive X-ray spectrometry analysis showed the purity of the prepared samples. The ZnO nanoparticles decorated graphene sheets were clearly visible in the field emission scanning electron micrograph. Raman mapping was employed to analyze the homogeneity of the prepared samples. The diffuse-reflectance spectra clearly indicated that the formation of GZ composites promoted the absorption in the visible region also. The photocatalytic activity of ZnO and GZ composites was studied by the photodegradation of Methylene blue dye. The results revealed that the GZ composites exhibited a higher photocatalytic activity than pristine ZnO. Hence, we proposed a simple wet chemical method to synthesize GZ composite and its application on photocatalysis was demonstrated.

Photocatalysts workable under direct sunlight are the safe and cost-effective option for water purification. The nanocomposites of strontium oxide and zinc oxide (SZ NCs) were synthesized using coprecipitation method. The respective precursors of SZ NCs were subjected to alkaline hydrolysis and subsequently thermally treated to yield SZ NCs. The SZ NCs with different ZnO composition was synthesized by varying the concentration of ZnO precursor from 0.2 to 1 M. The structural properties of SZ NCs evaluated using X-Ray diffraction (XRD), Thermogravimetric analysis (TGA), and Differential thermal analysis DTA). The optical properties of SZ NCs studied using ultraviolet–visible (UV–Vis) spectroscopic study. The trend observed in the intensity of XRD peaks indicated the occurrence of Zn doping in the crystalline lattice of SrO and the formation of SrO–ZnO composite. Upon incorporation of 1 M of ZnO precursor, the grain size of the SrO was decreased from 49.3 to 27.6 nm. The weight loss in the thermal analysis indicates the removal of carbonates from the sample upon heating and shows the formation of an oxide structure. UV–Vis spectra confirmed that the presence of SrO enhanced the sunlight absorption of SZ NCs. The increase in the composition of ZnO precursors increased the bandgap of SrO (2.09 eV) to the level of ZnO (3.14 eV). SZ NCs exhibited heterostructure morphology, where the nanosized domains with varying shapes (layered and rod-like) were observed. Under direct sunlight conditions, SZ NCs prepared using 1 M/0.6 M of SrO/ZnO precursors exhibited 15–20 % higher photocatalytic efficiency than neat SrO and ZnO. In precise, 1 mg of this SZ NC was degraded 98 % of malachite green dye dissolved in water (10 ppm) under direct sunlight. Additionally, the thermal stability results showed that 18 % decomposition was obtained due to the degradation impurities in SrO/ZnO catalysts and the XRD results revealed that no structural change is obtained in SrO/ZnO photocatalysts after stability test. The SZ NCs can be effectively used as safe and economic sunlight photocatalysts for water purification in remote areas without the electricity.

Cubic and hexagonal phase zinc titanate (ZT) nanoparticles were synthesized via simple chemical precipitation method. The graphene-zinc titanate (GZT) nanocomposites were prepared by using the synthesized ZT nanoparticles and graphene oxide as precursors. The synthesized materials were characterized by various spectroscopic techniques. The agglomerated ZT nanoparticles anchored on graphene sheets are clearly visible in the field emission scanning electron micrograph (FE-SEM) image. Raman mapping of the GZT nanocomposites revealed the homogeneity and distribution of ZT nanoparticles on the surface of graphene. The UV–visible absorption and photoluminescence spectra of the samples suggest that the GZT nanocomposites can be used as efficient photocatalysts to remove organic dye from water. The photocatalytic activity of the synthesized photocatalysts was evaluated by the photodegradation of methylene blue dye under sunlight irradiation. The enhanced absorption in the visible region of the GZT samples compared to the ZT samples played a vital role during the photocatalysis. The hexagonal phase GZT nanocomposite displayed remarkable photocatalytic activity compared to the bare ZT nanoparticles. The possible electron transfer mechanism for graphene-ZT interface during the photocatalysis process is also proposed. Furthermore, the reusability and stability tests for the prepared photocatalysts were made and reported.