Cyanidation is the main method used to extract gold from gold raw materials; however, a serious problem with this method is the low leaching rate. In order to improve gold leaching, the intensification behavior of mercury ions on gold cyanide leaching, for two types of materials, sulphide gold concentrate and oxide gold ore, was investigated. The results showed that mercury ions, with only a 10⁻⁵ M dosage, could significantly intensify leaching and gold recovery. The dissolution behavior of gold plate was also intensified by 10⁻⁵ M mercury ions. Microstructure analysis showed that mercury ions intensified the cyanidation corrosion of the gold surface, resulting in a loose structure, where a large number of deep ravines and raised particles were evident across the whole gold surface. The loose structure added contact surface between the gold and cyanide, and accelerated gold dissolution. Moreover, mercury ions obstructed the formation of insoluble products, such as AuCN, Au(OHCN), and Au(OH)_x, that lead to a passivation membrane on the gold surface, reducing contact between the gold and cyanide. These effects, brought about by mercury ions, change the structure and product of the gold surface during gold cyanidation and promote gold leaching.

Pyrolysis and combustion behaviors of three coals (A, B, and C coals) were investigated and their combustion kinetics were calculated by the Freeman–Carroll method to obtain quantitative insight into their combustion behaviors. Moreover, the effects of coal size, air flow, oxygen content, and heating rate on coal combustion behaviors were analyzed. Results showed that the three coals have a similar trend of pyrolysis that occurs at about 670 K and this process continuously proceeds along with their combustion. Combustion characteristics and kinetic parameters can be applied to analyze coal combustion behaviors. Three coals having combustion characteristics of suitable ignition temperature (745–761 K), DTG_max (14.20–15.72%/min), and burnout time (7.45–8.10 min) were analyzed in a rotary kiln. Combustion kinetic parameters provide quantitative insights into coal combustion behavior. The suitable particle size for coal combustion in a kiln is that the content of less than 74 μm is 60% to 80%. Low activation energy and reaction order make coal, especially C coal, have a simple combustion mechanism, great reactivity, be easily ignited, and a low peak temperature in the combustion state. Oxygen-enrichment and high heating rates enhance coal combustion, increasing combustion intensity and peak value, thus shortening burnout time.

Gold cyanide leaching is inefficient with conventional cyanidation. Bismuth ions can improve the efficiency of gold cyanidation by intensifying gold dissolution. The electrochemical behavior, structure information, and surface product of gold anodic dissolution were studied during the intensification of bismuth ions on gold cyanide leaching. The electrochemical analysis showed that the bismuth ions can not only improve anode current density, but also make gold dissolve at a lower potential, increase the corrosion current and intensify gold anodic dissolution. The microstructure analysis showed that bismuth ions intensified the cyanide corrosion of the gold surface, causing a large number of loose honeycombs, gullies, pits, and large holes on the gold surface. The XPS, FT-IR, and Raman analysis showed that there is weak information of C≡N in the spectrum of Bi intensification contrasting to that of conventional cyanidation. Cyanide compounds may be the insoluble AuCN_ads, which does not deposit on the surface of gold plate after Bi intensification cyanidation. The insoluble intermediate AuCN_ads is likely to react promptly with CN^- to form soluble Au(CN ${)}_2^{-}$ , making less insoluble AuCN_ads deposits on the gold surface. Therefore, bismuth ions can promote the dissolution of insoluble AuCN_ads, prevents its passivation film to cover around the gold plate, keeps cyanide good contact with gold, and finally accelerates the cyanide dissolution of gold.