A new temperature stress test machine (TSTM) was developed to improve temperature control accuracy and efficiency. As there is no uniform standard for the threshold value of TSTM, quite different threshold values are used in the test, which results in the influences of the threshold value on the evaluation of thermal stresses and crack risk of concrete not being determined. To illustrate the importance of an appropriate threshold value, different threshold values were used to evaluate the influences on the thermal stresses and cracking resistance of concrete specimens under a complete restraint test with semi-adiabatic temperature development. The results show that the maximum compressive stress of a concrete specimen with a threshold value 3 με was slightly larger than that of 1.5 με when the growth rate of tensile stress of the concrete specimen with the threshold value 3 με was slightly greater than that of concrete specimen with the threshold value 1.5 με. Based on the combination of crack risk coefficient and restraint degree, a new system for evaluating the crack resistance of concrete was proposed, in which different threshold values were used to estimate their influences on the crack risk of concrete. Thus, an appropriate range of threshold values could be determined.

Internal curing with super-absorbent polymer (SAP) has been developed to improve autogenous shrinkage of high performance concrete (HPC) in recent years. However, studies about effect of SAP on the tensile creep of HPC seem insufficient. In this paper, a series of concrete ring tests were conducted to investigate effect of SAP on the tensile creep of early-age HPC. Meanwhile, shrinkage and mechanical properties of concrete with SAP were also investigated. Results show that tensile creep coefficient of concrete with SAP was similar to that of reference concrete with same basic w/c, but lower compared with that of reference concrete with same total w/c.

For concrete under short-term loading, effect of reinforcement on concrete crack resistance capability is usually negligible; however, recent research results show that extension of this viewpoint to concrete under long-term loading (temperature variation) may be unsuitable. In order to investigate this phenomenon, this paper presents the experimental and analytical results of early-age reinforced concrete temperature stress development under uniaxial restraint. The experiments were carried out on a temperature stress testing machine (TSTM). Experimental results show that the coupling of reinforcement and concrete creep behavior influenced the concrete temperature stress development, and nearly 16% of concrete stress was reduced in the current research. Moreover, the cracking time of reinforced concrete was also delayed. Finally, based on the principle of superposition, analytical simulations of effect of reinforcement on concrete temperature stress have been performed.