Mean pore size is an essential aspect of scaffolds for tissue-engineering. If pores are too small cells cannot migrate in towards the center of the construct limiting the diffusion of nutrients and...

Crosslinking and the resultant changes in mechanical properties have been shown to influence cellular activity within collagen biomaterials. With this in mind, we sought to determine the effects of crosslinking on both the compressive modulus of collagen-glycosaminoglycan scaffolds and the activity of osteoblasts seeded within them. Dehydrothermal, 1-ethyl-3-3-dimethyl aminopropyl carbodiimide and glutaraldehyde crosslinking treatments were first investigated for their effect on the compressive modulus of the scaffolds. After this, the most promising treatments were used to study the effects of crosslinking on cellular attachment, proliferation, and infiltration. Our experiments have demonstrated that a wide range of scaffold compressive moduli can be attained by varying the parameters of the crosslinking treatments. 1-Ethyl-3-3-dimethyl aminopropyl carbodiimide and glutaraldehyde treatments produced the stiffest scaffolds (fourfold increase when compared to dehydrothermal crosslinking). When cells were seeded onto the scaffolds, the stiffest scaffolds also showed increased cell number and enhanced cellular distribution when compared to the other groups. Taken together, these results indicate that crosslinking can be used to produce collagen–glycosaminoglycan scaffolds with a range of compressive moduli, and that increased stiffness enhances cellular activity within the scaffolds.

Bone tissue engineering has emerged as one of the leading fields in tissue engineering and regenerative medicine. The success of bone tissue engineering relies on understanding the interplay between progenitor cells, regulatory signals, and the biomaterials/scaffolds used to deliver them--otherwise known as the tissue engineering triad. This review will discuss the roles of these fundamental components with a specific focus on the interaction between cell behaviour and scaffold structural properties. In terms of scaffold architecture, recent work has shown that pore size can affect both cell attachment and cellular invasion. Moreover, different materials can exert different biomechanical forces, which can profoundly affect cellular differentiation and migration in a cell type specific manner. Understanding these interactions will be critical for enhancing the progress of bone tissue engineering towards clinical applications.

The pore structure of three-dimensional scaffolds used in tissue engineering has been shown to significantly influence cellular activity. As the optimal pore size is dependant on the specifics of the tissue engineering application, the ability to alter the pore size over a wide range is essential for a particular scaffold to be suitable for multiple applications. With this in mind, the aim of this study was to develop methodologies to produce a range of collagen–glycosaminoglycan (CG) scaffolds with tailored mean pore sizes. The pore size of CG scaffolds is established during the freeze-drying fabrication process. In this study, freezing temperature was varied (−10°C to −70°C) and an annealing step was introduced to the process to determine their effects on pore size. Annealing is an additional step in the freeze-drying cycle that involves raising the temperature of the frozen suspension to increase the rate of ice crystal growth. The results show that the pore size of the scaffolds decreased as the freezing temperature was reduced. Additionally, the introduction of an annealing step during freeze-drying was found to result in a significant increase (40%) in pore size. Taken together, these results demonstrate that the methodologies developed in this study can be used to produce a range of CG scaffolds with mean pore sizes from 85 to 325 μm. This is a substantial improvement on the range of pore sizes that were possible to produce previously (96–150 μm). The methods developed in this study provide a basis for the investigation of the effects of pore size on both in vitro and in vivo performance and for the determination of the optimal pore structure for specific tissue engineering applications.