Arrays of silver nanowires have received increasing attention in a variety of applications such as surface-enhanced Raman scattering (SERS), plasmonic biosensing and electrode for photoelectric devices. However, until now, large scale fabrication of device-suitable silver nanowire arrays on supporting substrates has seen very limited success. Here we show the synthesis of free-standing silver nanowire arrays on indium-tin oxide (ITO) coated glass by pulsed electrodeposition into anodic aluminum oxide (AAO) templates. We use an in situ oxygen plasma cleaning process and a sputtered Ti layer to enhance the adhesion between the template and ITO glass. An ultrathin gold layer (2 nm) is deposited as a nucleation layer for the electrodeposition of silver. An unprecedented high level of uniformity and control of the nanowire diameter, spacing and length has been achieved. The absorption measurements show that the free-standing silver nanowire arrays possess tunable plasmonic resonances.

Sonodynamic therapy (SDT) is a promising treatment method for solid tumors. However, the high interstitial fluid pressure (IFP) in tumor tissues limits the accumulation of sonosensitizers. In the present study, microbubbles ultrasonic cavitation was used to regulate the tumor’s IFP and evaluate SDT effects. Rabbit VX2 tumor tissues were treated with microbubbles ultrasonic cavitation. The IFP of different tumor parts before and after cavitation was measured by the WIN method. The accumulation of the sonosensitizers hematoporphyrin monomethyl ether (HMME) in tumor tissues was observed using an ultramicro spectrophotometer and laser confocal microscope. Then, tumor-bearing rabbits were treated with SDT once a week for eight weeks and the therapeutic effect was evaluated. After microbubbles ultrasonic cavitation treatment, the tumor’s IFP decreased and the HMME concentration increased. We concluded that microbubbles ultrasonic cavitation can increase HMME accumulation in rabbit VX2 tumors and increase SDT therapeutic effects.

An electrode structured with a TiO₂/Ag/TiO₂ (TAT) multilayer as indium tin oxide (ITO) replacement with a superior thermal stability has been successfully fabricated. This electrode allows to directly tune the optical cavity mode towards maximized photocurrent generation by varying the thickness of the layers in the sandwich structure. This enables tailored optimization of the transparent electrode for different organic thin film photovoltaics without alteration of their electro-optical properties. Organic photovoltaic featuring our TAT multilayer shows an improvement of ∼12% over the ITO reference and allows power conversion efficiencies (PCEs) up to 8.7% in PTB7:PC₇₁BM devices.

Halide perovskites have emerged as a compelling material for a broad range of optoelectronic applications, including light-emitting diodes, phototransistors, light-sensing and imaging systems. To enable practical application and compatibility with existing consumer electronics, they must be integrated with heterogeneous electronic platforms, such as complementary metal-oxide-semiconductor chips or thin-film transistors. Such integration is pivotal for transitioning perovskite technologies from laboratory demonstrations to commercial applications. In this perspective, we summarize recent progress in the system-level integration of perovskite optoelectronics with driving backplanes, compare key performance metrics with industrial benchmarks, discuss major challenges, and outline future directions and application prospects for perovskite optoelectronics.

Plasmonic metamaterials enable extraordinary manipulation of key constitutive properties of light at a subwavelength scale and thus have attracted significant interest. Here, we report a simple and convenient nanofabrication method for a novel meta-device by glancing deposition of gold into anodic aluminum oxide templates on glass substrates. A methodology with the assistance of ellipsometric measurements to examine the anisotropy and optical activity properties is presented. A tunable polarization conversion in both transmission and reflection is demonstrated. Specifically, giant broadband circular dichroism for reflection at visible wavelengths is experimentally realized by oblique incidence, due to the extrinsic chirality resulting from the mutual orientation of the metamaterials and the incident beam. This work paves the way for practical applications for large-area, low-cost polarization modulators, polarization imaging, displays, and bio-sensing.