We present two different ways to fabricate nitrogen-doped graphene (N-graphene) and demonstrate its use as a metal-free catalyst to study the catalytic active center for the oxygen reduction reaction (ORR). N-graphene was produced by annealing of graphene oxide (G-O) under ammonia or by annealing of a N-containing polymer/reduced graphene oxide (RG-O) composite (polyaniline/RG-O or polypyrrole/RG-O). The effects of the N precursors and annealing temperature on the performance of the catalyst were investigated. The bonding state of the N atom was found to have a significant effect on the selectivity and catalytic activity for ORR. Annealing of G-O with ammonia preferentially formed graphitic N and pyridinic N centers, while annealing of polyaniline/RG-O and polypyrrole/RG-O tended to generate pyridinic and pyrrolic N moieties, respectively. Most importantly, the electrocatalytic activity of the catalyst was found to be dependent on the graphitic N content which determined the limiting current density, while the pyridinic N content improved the onset potential for ORR. However, the total N content in the graphene-based non-precious metal catalyst does not play an important role in the ORR process.

We report the largely improved electrochemical capacitance of polypyrrole-derived microporous carbon nanospheres (MCNs, 80–100 nm in diameter) containing nitrogen functional groups. We have investigated the electrochemical properties of precursor polypyrrole nanospheres (PNs, with a high N/C ratio and low surface area) and as-derived carbon nanospheres (CNs, with a moderate N/C ratio and low surface area) prepared by carbonizing PNs at different temperatures, and MCNs (with a low N/C ratio and high surface area) obtained by chemical activation of CNs. The samples are thoroughly characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman spectroscopy, thermogravimetric analysis (TGA), nitrogen sorption, elemental analysis, and X-ray photoelectron spectroscopy (XPS). It is found that MCNs with a high surface area and N-doping species exhibit much better capacitive performance compared to the PNs and CNs, and commercial carbon blacks (XC-72 and BP2000) as well. The MCN sample gives a reversible specific capacitance of ∼240 F g⁻¹ for 3000 cycles in aqueous media as a result of combined advantages of high electrochemical activity of doped heteroatoms (N and O) and accessible well-developed porosity, demonstrating the promising use in high-energy-density supercapacitors.