Fe-based alloys are commonly used in almost every sector of human life. For different reasons, the surfaces of the real parts are prepared using different methods, e.g., mirror-like polishing, grit-blasting, etc. The purpose of the present work is to answer the question how the surface preparation influences the oxidation behavior of Fe-based alloys. To answer this question, a high-purity model alloy, Fe–5 wt%Al, was isothermally oxidized in a thermogravimetrical furnace. The post-exposure analysis included SEM/EDS (WDS) and XRD. The surface roughness was determined by a contact and laser profilometer. The obtained results demonstrate that the mechanical surface preparation influences oxidation kinetics as well as the microstructure of the oxide scale formed on the alloy at both studied temperatures. Namely, polishing and grinding caused local formation of Fe-rich nodules and sub-layer of protective Al₂O₃. In contrast, grit-blasting leads to the formation of a thick outer Fe-oxide and internal aluminum nitridation. A significant increase in the oxidation rate of the material after grit-blasting was attributed to grain refinement in the near-surface region, resulting in an increase in easy diffusion paths, namely grain boundaries.

The effects of surface preparations on oxidation kinetics and oxide scale morphology for the commercially available Ni-based superalloy IN 713C have been investigated. The ground and polished samples were exposed in air at 800-1100 °C. The ground specimens were found to demonstrate lower oxidation kinetics compared to those after polishing. The grinding also affected the oxide scale morphology, resulting in a protective alumina scale, while the polished samples developed Ni-/Cr-rich mixed oxides on the surface. Better oxidation resistance of the ground surfaces is related to a higher concentration of defects in the near-surface region introduced by cold working. These defects facilitate the outward transport of the scale-forming element Al and thus are beneficial for protective oxidation. The oxidation mechanism at lower temperatures was introduced. The model based on the generalized Darken method and multiphase approximation was proposed.