This study investigates the effects of incorporating recycled coarse aggregates (RCAs) at different substitution rates on the mechanical and fracture properties of recycled aggregate concrete (RAC). Four concrete mixtures were prepared: a reference mixture using natural coarse aggregates (NCAs) and three RAC mixtures in which 30%, 60%, and 100% of the NCA mass was replaced with RCAs. The RAC mixtures were compared to natural aggregate concrete (NAC) in terms of compressive strength, splitting tensile strength, modulus of elasticity, hydration rate, water-accessible porosity, pore size distribution, post-peak behavior, and fracture energy. The results show that as the RCA substitution rate increases, the RAC porosity rises and its modulus of elasticity decreases. However, the compressive strength and splitting tensile strength remain comparable to, or even exceed, those of NAC, with optimal performance observed at a 60% substitution rate. This optimal behavior can be attributed to a more favorable pore distribution and an increased hydration rate. For an equivalent strength class, RAC with up to 60% RCA substitution exhibits post-peak behavior and fracture energy comparable to NAC. However, at a 100% substitution rate, the behavior becomes more brittle, and fracture energy decreases by 23.20%.

This study focuses on the use of dredged sediment (SD) from the dam for the synthesis of a geopolymer. The samples investigated in this work were prepared by mixing micronized and calcined sediment and ground granulated blast furnace slag (GGBFS), at different percentages (10%, 20%, 30%, 40%, and 50%). Furthermore, the influence of the molarity of the NaOH solution, which was used as an activator, as well as the impacts of the (SD/GGBFS) and (SiO₂/Al₂O₃) ratios, and the use of different activator solutions, were also examined. In addition, the effects of the curing temperature and porosity were explored The results revealed that among the NaOH concentrations studied (6M, 8M, 10M, 12M, and 14M), 12M was identified as the optimal concentration, and the optimum SD/GGBFS ratio was 70/30. In addition, variation of the ratio (SiO₂/Al₂O₃) allowed the identification of specific proportions for different binders. Indeed, a ratio (SiO₂/Al₂O₃) equal to 4.45 offered an optimum compressive strength of 24.86 MPa, which is significantly higher than the 13.7 MPa obtained for the geopolymer based on sediment with a SiO₂/Al₂O₃ ratio of 3.12 and 12M NaOH. Moreover, the curing temperature of 40 °C, for a period of 48 h, gave a mechanical strength value that was higher than that obtained at room temperature. Similarly, the optimal formulations led to a significant reduction in total porosity, especially when the molarity of the NaOH solution was high, with a GGBFS percentage of 30% achieving an optimal porosity value of 12.5%. Likewise, the X-ray diffraction, infrared spectroscopy (FTIR), and scanning electron microscopy (SEM) analyses confirmed the formation of geopolymers with a compact structure, which paves the way for the development of innovative and sustainable eco-construction materials with a low-carbon footprint.