Introduction. Protozoal intestinal infections are quite common in the modern world. They cause severe clinical manifestations, and in some cases, more often, in countries with a hot climate, lead to death. This is due to the ability of the pathogen to enter the human body through water, fecal-oral or alimentary routes. In this regard, the development of a new safe and effective enterosorbent for protozoal diseases affecting the gastrointestinal tract is relevant.Aim: To study the effectiveness of the combined enterosorbent based on hydroxyapatite and compare the effectiveness of its use with colloidal silicon dioxide (Polysorb) in relation to protozoa (eimeria) in an experiment on rabbits.Material and Methods. The development of a combined enterosorbent based on calcium hydroxyapatite and experimental treatment of laboratory animals (rabbits - 40 animals) infected with protozoal disease - eimeriosis was carried out. Four groups were formed: healthy control, infected control, infected experimental group, infected comparison group (comparison drug – Polysorb). The therapy was carried out for 5 days. The drugs were administered orally.Results. It is shown that the use of a combined enterosorbent based on calcium hydroxyapatite in a daily dose of 0.05 g per 1 kg of body weight led to a decrease in the intensity of invasion of the gastrointestinal tract of rabbits by oocysts by 80% compared with the control, and the use of colloidal silicon dioxide in a daily dose of 0.1-0.2 g per 1 kg of body weight by 49% compared with control.Conclusion. The combined preparation based on calcium hydroxyapatite effectively reduces the intensity of invasion by oocysts of the gastrointestinal tract of rabbits in the experiment. Its intensity efficiency exceeds the intensity of colloidal silicon dioxide by 31%.

Повышенные требования к полимерным материалам и расширение областей их применения создают предпосылки создания новыхбиокомпозиционных материалов. Наиболее перспективной матрицей для биокомпозиционного материала является 2-гидроксипропионовая (молочная) кислота, уникальные возможности которой проявляются в результате модификации неорганическими минеральными наполнителями нанометрического размера. Особенно ценным является сочетание в данном полимере таких свойств как биоразлагаемость и биосовместимость. Наноструктурированные композиционные материалы, состоящие из полимолочной кислоты и минеральных наполнителей, приобретают существенное улучшение свойств по сравнению со свойствами чистого полимера.Методом полива формовочных растворов получены биоразлагаемые пленки, содержащие в составе слоистый природный минерал из класса метасиликатов. В качестве растворителя для приготовления формовочного раствора использовали трихлорметан. Изучены структура и свойства наноструктурированного термопластичного композита. Показано, что наполнитель равномерно распределяется в структуре полимера, влияет на размеры кристаллических образований, размеры кристаллитов увеличиваются. Введение наноструктурирующего минерала в биополимер повышает термостойкость композита, что обусловлено высокой устойчивостью к действию повышенных температур исходного микроармирующего минерального наполнителя, который не разлагается до температуры 1000-1100 0С. Установлено влияние слоистого природного минерала из класса метасиликатов на деформационно-прочностные свойства биокомпозита: сохраняется прочность и незначительно снижается относительное удлинение при разрыве материала. Способность к биоразложению и очень низкая токсичность позволяют использовать наноструктурированный композиционный материал на основе 2-гидроксипропионовой (молочной) кислоты в биомедицинских, фармацевтических, экологических и промышленных областях. Разработка биоразлагаемого композиционного материала позволит решить актуальные отечественные проблемы полимеров медицинскогоназначения.

Radiation transfer in layers of densely packed aggregates of hydroxyapatite nanoparticles was studied for a spectral range from 300 to 1100 nm using diffuse reflectance measurements and the modeling of the light transfer properties of the layers. The studied samples of dispersed biogenic hydroxyapatite were obtained from animal bone material (bovine bones) using fast pyrolysis followed by grinding and pressing into tablets. A distinctive feature is the high reflectivity (high albedo) of the obtained samples, which is practically independent of the wavelength in the studied spectral range and comparable to the reflectivity of the diffuse reflectance standard based on Spectralon. The modeling of the light transfer properties of the studied samples within the framework of the effective medium theory (using coherent potential approximation) made it possible to establish the weak dependence of the mean scattering-free path and the mean transport-free path of light propagation in the medium on the wavelength, which is consistent with the features observed in the experiment. Possible prospects for the use of nanostructured hydroxyapatite as photonic material are discussed.

The optical properties of a composite material consisting of close-packed (with a volume fraction of about 0.4) polydisperse bio-hydroxyapatite particles in a sodium silicate matrix are examined in the near UV, visible and near IR ranges (between 0.3 μm and 1.0 μm) based on measured diffuse reflectance spectra and theoretical data. The theoretical analysis of wavelength-dependent light transfer in the composite was performed using Monte Carlo simulations and the coated coherent potential approximation as a modification of the frequency-dependent effective medium theory. The recovery of the effective values of the scattering anisotropy parameter for the studied system at various wavelengths based on a comparison of the measured and calculated diffuse reflectance of composite layers of different thicknesses made it possible to assume a decrease in this parameter from 0.9 to 0.4 under the transition from the near UV to the near IR interval. The negative dispersion of the wavelength dependences of the diffuse reflectance observed in the experiments is considered in relation to the negative dispersions of the scattering mean free path and scattering anisotropy expected for the dependent scattering regime. Possible applications of hydroxyapatite-based composites as photonic media with a disordered close-packed structure are discusse