The aim of this paper is to compare the flexural performance of reinforced concrete (RC) beams strengthened with textile-reinforced mortar (TRM) and fibre-reinforced polymers (FRP). The investigated parameters included the strengthening material, namely TRM or FRP; the number of TRM/FRP layers; the textile surface condition (coated and uncoated); the textile fibre material (carbon, coated basalt or glass fibres); and the end-anchorage system of the external reinforcement. Thirteen RC beams were fabricated, strengthened and tested in four-point bending. One beam served as control specimen, seven beams strengthened with TRM, and five with FRP. It was mainly found that: (a) TRM was generally inferior to FRP in enhancing the flexural capacity of RC beams, with the effectiveness ratio between the two systems varying from 0.46 to 0.80, depending on the parameters examined, (b) by tripling the number of TRM layers (from one to three), the TRM versus FRP effectiveness ratio was almost doubled, (c) providing coating to the dry textile enhanced the TRM effectiveness and altered the failure mode; (d) different textile materials, having approximately same axial stiffness, resulted in different flexural capacity increases; and (e) providing end-anchorage had a limited effect on the performance of TRM-retrofitted beams. Finally, a simple formula proposed by fib Model Code 2010 for FRP reinforcement was used to predict the mean debonding stress developed in the TRM reinforcement. It was found that this formula is in a good agreement with the average stress calculated based on the experimental results when failure was similar to FRP-strengthened beams

This paper presents an extended experimental study on the bond behaviour between textile-reinforced mortar (TRM) and concrete substrates. The parameters examined include: (a) the bond length (from 50 mm to 450 mm); (b) the number of TRM layers (from one to four); (c) the concrete surface preparation (grinding versus sandblasting); (d) the concrete compressive strength (15 MPa or 30 MPa); (e) the textile coating; and (f) the anchorage through wrapping with TRM jackets. For this purpose, a total of 80 specimens were fabricated and tested under double-lap direct shear. It is mainly concluded that: (a) after a certain bond length (between 200 mm and 300 mm for any number of layers) the bond strength marginally increases; (b) by increasing the number of layers the bond capacity increases in a non-proportional way, whereas the failure mode is altered; (c) concrete sandblasting is equivalent to grinding in terms of bond capacity and failure mode; (d) concrete compressive strength has a marginal effect on the bond capacity; (e) the use of coated textiles alters the failure mode and significantly increases the bond strength; and (f) anchorage of TRM through wrapping with TRM jackets substantially increases the ultimate load capacity

The flexural behaviour of RC beams strengthened with TRM and FRP composites was experimentally investigated and compared both at ambient and high temperatures. The investigated parameters were: (a) the strengthening material, namely TRM versus FRP, (b) the number of strengthening layers, (c) the textile surface condition (dry and coated), (d) the textile material (carbon, basalt or glass fibres) and (e) the end-anchorage of the flexural reinforcement. A total of 23 half-scale beams were constructed, strengthened in flexure and tested to assess these parameters and the effectiveness of the TRM versus FRP at high temperatures. TRM exhibited excellent performance as strengthening material in increasing the flexural capacity at high temperature; in fact, TRM maintained an average effectiveness of 55%, compared to its effectiveness at ambient temperature, contrary to FRP which totally lost its effectiveness when subjected to high temperature. In specific, from the high temperature test it was found that by increasing the number of layers, the TRM effectiveness was considerably enhanced and the failure mode was altered; coating enhanced the TRM effectiveness; and the end-anchorage at high temperature improved significantly the FRP and marginally the TRM effectiveness. Finally, the formula proposed by the Fib Model Code 2010 was used to predict the mean debonding stress in the TRM reinforcement, and using the experimental results obtained in this study, a reduction factor to account for the effect of high temperature on the flexural strengthening with TRM was proposed

The use of fibre reinforced polymers (FRP) as a means of external reinforcement for strengthening the existing reinforced concrete (RC) structures nowadays is the most common technique. However, the use of epoxy resins limits the effectiveness of FRP technique, and therefore, unless protective (thermal insulation) systems are provided, the bond capacity at the FRP-concrete interface will be extremely low above the glass transition temperature (Tg). To address problems associated with epoxies and to provide cost-effectiveness and durability of the strengthening intervention, a new composite cement- based material, namely textile-reinforced mortar (TRM) has been developed the last decade. This paper for the first time examines the bond performance between the TRM and concrete interfaces at high temperatures and, also compares for the first time the bond of both FRP and TRM systems to concrete at ambient and high temperatures. The key parameters investigated include: (a) the matrix used to impregnate the fibres, namely resin or mortar, resulting in two strengthening systems (TRM or FRP), (b) the level of high temperature to which the specimens are exposed (20, 50, 75, 100, and 150 °C) for FRP-reinforced specimens, and (20, 50, 75, 100, 150, 200, 300, 400, and 500 °C) for TRM-strengthened specimens, (c) the number of FRP/TRM layers (3 and 4), and (d) the loading conditions (steady state and transient conditions). A total of 68 specimens (56 specimens tested in steady state condition, and 12 specimens tested in transient condition) were constructed, strengthened and tested under double- lap direct shear. The result showed that overall TRM exhibited excellent performance at high temperature. In steady state tests, TRM specimens maintained an average of 85% of their ambient bond strength up to 400 °C, whereas the corresponding value for FRP specimens was only 17% at 150 °C. In transient test condition, TRM also outperformed over FRP in terms of both the time they maintained the applied load and the temperature reached before failure

The issue of upgrading and strengthening the reinforced concrete (RC) infrastructure has become of great importance. Recently, textile-reinforced mortar (TRM) was used in the field of structural strengthening. In the current study, using of TRM for flexural retrofitting of one-way reinforced concrete (RC) slabs was experimentally and theoretically investigated. The parameters examined included; the number of TRM layers (1, 3, 5 layers) and the strengthening configuration fully and partially). For this purpose, eight specimens were prepared and tested under three points- loading up to failure. The result showed that the TRM increases substantially the flexural capacity of RC slabs. The highest flexural capacity increase recorded was 103 %. It was also noted that increasing the number of retrofitting layers resulted in different increases in the flexural capacity. It was also shown that the strengthening configuration plays an important role in the effectiveness of the technique. The fully covered approach showed higher loading capacity than the partial cover technique provided that the same TRM layer is applied. Finally, the ultimate moment of the strengthened specimens was calculated theoretically and compared with that obtained experimentally. The results of calculations showed a good agreement between the theoretical and experimental results.