We investigate the theory of cancellation by interference between the absorption of three fundamental laser photons and one third-harmonic photon. The theory is formulated in terms of the density matrix so as to take detunings, dephasing, and and laser bandwidth into account. The result is a theory of cancellation for finite detuning that explains how four-photon resonances can be canceled by a three-photon mechanism, if there is an atomic level at near three-photon resonance. We obtain explicit conditions for this to happen, and perform calculations pertaining to a recent experiment [D. Charalambdis et al., Phys. Rev. A (to be published)] where cancellation of 4+1 resonantly enhanced multiphoton ionization has been observed.

The effect of mass transport on the growth characteristics of large-area vapor-grown carbon nanofibers (CNFs) was investigated by adjusting the substrate deposition angle (α). The catalyst precursor solution was coated onto one side of a 2D porous carbon paper substrate via a decal printing method. The results showed that the CNFs were grown on only one side of the substrate and α was found to significantly affect the growth uniformity. At α = 0°, the growth thickness, the density, the microstructure and the yield of the CNF film were uniform across the substrate surface, whereas the growth uniformity decreased with increasing α, suggesting that the large-area CNF deposition processes were mass-transport-controlled. Computational fluid dynamics simulations of the gas diffusion processes revealed the homogeneous distributions of the carbon-source-gas concentration, pressure, and velocity near the substrate surface at α = 0°, which were the important factors in achieving the mass-transport-limited uniform CNF growth. The homogeneity of the field distributions decreased with increasing α, in accordance with the variation in the growth uniformity with α. When used as a micro-porous layer, the uniform CNF film enabled higher proton exchange membrane fuel cell performance in comparison with commercial carbon black by virtue of its improved electronic and mass-transport properties confirmed by the electrochemical impedance spectroscopy results.

The corrosion properties of 316L stainless steel (316L SS) alloy within molten NaCl-KCl salt were explored through a static immersion experiment carried out at 700 °C under Ar flow for 25, 50, 100, 200, and 400 h. The loss in weight of the corroded 316L SS alloy increased from 0.06 to 1.71 mg/cm², while the maximum corrosion depth increased from 1.71 to 14.09 μm. However, the corrosion rate initially increased from 27.54 μm/year to 93.45 μm/year and then decreased to 47.22 μm/year as the soaking time was increased from 25 to 400 h. The impurities in the molten salts produced corrosive Cl₂ and HCl, which corroded the 316L SS matrix. The accelerated selective Cr dissolution with small amounts of Fe and Ni resulted in intergranular corrosion as the time of corrosion was increased. The depletion depths for Ni, Cr, and Fe at 400 h were found to be 0.87 μm, 3.94 μm, and 1.47 μm, respectively. The formation of Cr and Fe oxides might potentially play a vital role. The grain boundary and outward diffusion of Mo may prevent the outward diffusion of Cr, thereby mitigating alloy corrosion. Therefore, molten chloride salt purification and the selection of stainless steel are crucial for developing future concentrated solar power technologies. The findings of this study provide guidelines for the use of 316L SS in NaCl-KCl salt at high temperatures.