Photostability of organic photovoltaic devices represents a key requirement for the commercialization of this technology. In this field, ZnO is one of the most attractive materials employed as an electron transport layer, and the investigation of its photostability is of particular interest. Indeed, oxygen is known to chemisorb on ZnO and can be released upon UV illumination. Therefore, a deep analysis of the UV/oxygen effects on working devices is relevant for the industrial production where the coating processes take place in air and oxygen/ZnO contact cannot be avoided. Here we investigate the light-soaking stability of inverted organic solar cells in which four different solution-processed ZnO-based nanoparticles were used as electron transport layers: (i) pristine ZnO, (ii) 0.03 at %, (iii) 0.37 at %, and (iv) 0.8 at % aluminum-doped AZO nanoparticles. The degradation of solar cells under prolonged illumination (40 h under 1 sun), in which the ZnO/AZO layers were processed in air or inert atmosphere, is studied. We demonstrate that the presence of oxygen during the ZnO/AZO processing is crucial for the photostability of the resulting solar cell. While devices based on undoped ZnO were particularly affected by degradation, we found that using AZO nanoparticles the losses in performance, due to the presence of oxygen, were partially or totally prevented depending on the Al doping level.

Two conjugated donor–acceptor copolymers based on a benzodithiophene donor unit and a fluorinated quinoxaline acceptor unit, spaced with either thiophene or thieno[3,2-b]thiophene π-bridges, were designed and synthesized. The effect of different π-bridges and of the processing conditions on optical, electrical, morphological and photovoltaic properties of the polymer:fullerene blend films were investigated. The polymer containing the thieno[3,2-b]thiophene π-bridge (PBDTFQ-TT) showed a red-shifted absorption and an enhanced charge carrier mobility, as compared to its analogue with the thiophene π-bridge (PBDTFQ-T), due to its narrower optical gap (by ∼0.1 eV) and stronger inter-chain interactions, favored by the structural planarity and increased linearity of the polymer backbone, as also supported by DFT calculations. The blend of PBDTFQ-TT and PC₆₁BM ([6,6]-phenyl-C₆₁-butyric acid methyl ester), compared to the PBDTFQ-T:PC₆₁BM one processed under the same conditions (by blade-coating technique), showed greatly enhanced photovoltaic performance, with more than doubled power conversion efficiency (PCE up to 5.60% for the best device) due to the increased short-circuit current density and fill factor. However, similar PCEs were also achieved for PBDTFQ-T:PC₆₁BM-based devices by optimizing the processing conditions through the addition of 1,8-diiodooctane (DIO) as the solvent additive. Through morphological and electrical analysis of the films, produced with and without additive, it was observed that the addition of DIO greatly enhances the self-organization, and consequently the charge mobility, of the thiophene π-bridge-based polymer, while it was detrimental for the nanoscale morphology and photovoltaic performances of the thieno[3,2-b]thiophene π-bridge-based polymer in the corresponding blend.