Peri-implant fibrosis (PIF) increases the postsurgical risks after implantation and limits the efficacy of the implantable drug delivery systems (IDDS). Pirfenidone (PF) is an oral anti-fibrotic drug with a short (1100 μm in control groups) approaching the intact derma thickness value (302 ± 15 μm). In PLA@PF group, the implant biodegradation developed faster, while arginase-1 expression was suppressed in comparison with other groups. This study proves the feasibility of the local control of fibrotic response on implants via modulation of foreign body reaction with slowly biodegradable PF-loaded IDDS.

Scaffold-free in vitro organogenesis exploits the innate ability of cells to synthesise and deposit their own extracellular matrix to fabricate tissue-like assemblies. Unfortunately, cell-assembled tissue engineered concepts require prolonged ex vivo culture periods of very high cell numbers for the development of a borderline three-dimensional implantable device, which are associated with phenotypic drift and high manufacturing costs, thus, hindering their clinical translation and commercialisation. Herein, we report the accelerated (10 days) development of a truly three-dimensional (338.1 ± 42.9 μm) scaffold-free tissue equivalent that promotes fast wound healing and induces formation of neotissue composed of mature collagen fibres, using human adipose derived stem cells seeded at only 50,000 cells/cm² on an poly (N-isopropylacrylamide-co-N-tert-butylacrylamide (PNIPAM86-NTBA14) temperature-responsive electrospun scaffold and grown under macromolecular crowding conditions (50 μg/ml carrageenan). Our data pave the path for a new era in scaffold-free regenerative medicine.

Mature hypertrophic scars (HSs) remain a challenging clinical problem, particularly due to the absence of biologically relevant experimental models as a standard rabbit ear HS model only reflects an early stage of scarring. The current study aims to adapt this animal model for simulation of mature HS by validating the time of the scar stabilization using qualitative and quantitative criteria. The full-thickness skin and perichondrium excision wounds were created on the ventral side of the rabbit ears. The tissue samples were studied on post-operation days (PODs) 30, 60, 90 and 120. The histopathological examination and morphometry were applied in parallel with biochemical analysis of protein and glycosaminoglycans (GAGs) content and amino acid composition. The supramolecular organization of collagen was explored by differential scanning calorimetry. Four stages of the rabbit ear HS maturation were delineated and attributed with the histolomorphometrical and physicochemical parameters of the tissue. The experimental scars formed in 30 days but stabilized structurally and biochemically only on POD 90–120. This evidence-based model can be used for the studies and testing of new treatments of the mature HSs.

This study was aimed to design and characterise hybrid tissue-engineered constructs composed of osteoinducing polylactide-based scaffolds with multi-layered cellular biointerface for bone tissue reconstruction. Three-dimensional scaffolds with improved hydrophilic and osteoinducing properties were produced using the surface-selective laser sintering (SSLS) method. The designed scaffold pattern had dimensions of 8 × 8 × 2.5 mm and ladder-like pores (∼700 μ m in width). Hyaluronic acid-coated polylactide microparticles (∼100 μ m in diameter) were used as building blocks and water was used as the photosensitizer for SSLS followed by photocross-linking with Irgacure 2959 photoinitiator. Resulting scaffolds provided successful adhesion and expansion of human bone marrow mesenchymal stromal cells from a single-cell suspension. Induced calcium deposition by the cells associated with osteogenic differentiation was detected in 7–21 days of culturing in basal medium. The values were up to 60% higher on scaffolds produced at a higher prototyping speed under the experimental conditions. Innovative approach to graft the scaffolds with multi-layered cell sheets was proposed aiming to facilitate host tissue-implant integration. The sheets of murine MS-5 stromal cell line exhibited contiguous morphology and high viability in a modelled construct. Thus, the SSLS method proved to be effective in designing osteoinducing scaffolds suitable for the delivery of cell sheets.

Features of Polymeric Structures By Surface—Selective Laser Sintering of Polymer Particles Using Water as Sensitizer