The effect of large-strain cold-to-warm deformation on the microstructures and mechanical properties of various steels and alloys is critically reviewed. The review is mainly focused on the microstructure evolution, whereas the deformation textures are cursorily considered without detailed examination. The deformation microstructures are considered in a wide strain range, from early straining to severe deformations. Such an approach offers a clearer view of how the deformation mechanisms affect the structural changes leading to the final microstructures evolved in large strains. The general regularities of microstructure evolution are shown for different deformation methods, including conventional rolling/swaging and special techniques, such as equal channel angular pressing or torsion under high pressure. The microstructural changes during deformations under different processing conditions are considered as functions of total strain. Then, some important mutual relationships between the microstructural parameters, e.g., grain size vs. dislocation density, are revealed and discussed. Particular attention is paid to the mechanisms of microstructure evolution that are responsible for the grain refinement. The development of an ultrafine-grained microstructure during large strain deformation is considered in terms of continuous dynamic recrystallization. The regularities of the latter are discussed in comparison with conventional (discontinuous) dynamic recrystallization and grain subdivision (fragmentation) phenomenon. The structure–property relations are quantitatively represented for the structural strengthening, taking into account various mechanisms of dislocation retardation.

An effect of tempforming on the microstructure, the carbide precipitation, and the strengthening mechanisms of high-strength low-alloyed steel has been analyzed. The quenched steel was subjected to 1 h tempering at a temperature of 873 K, 923 K, or 973 K followed by plate rolling at the same temperature. Tempforming resulted in the formation of an ultrafine grained lamellar-type microstructure with finely dispersed carbides of (Nb,V)C, Fe₃C and Cr₂₃C₆. A decrease in tempforming temperature resulted in a reduction of the transverse grain size from 950 nm to 350 nm. Correspondingly, the size of Fe₃C/Cr₂₃C₆ particles decreased from 90 nm to 40 nm while the size of (Nb,V)C particles decreased from 17 nm to 4 nm. Refining the tempformed microstructure with a decrease in thetempforming temperature provided an increase in the yield strength from 690 MPa to 1230 MPa.

The microstructural mechanisms providing delamination toughness in high-strength low-alloyed steels are briefly reviewed. Thermo-mechanical processing methods improving both the strength and impact toughness are described, with a close relation to the microstructures and textures developed. The effect of processing conditions on the microstructure evolution in steels with different carbon content is discussed. Particular attention is paid to tempforming treatment, which has been recently introduced as a promising processing method for high-strength low-alloyed steel semi-products with beneficial combination of strength and impact toughness. Tempforming consists of large strain warm rolling following tempering. In contrast to ausforming, the steels subjected to tempforming may exhibit an unusual increase in the impact toughness with a decrease in test temperature below room temperature. This phenomenon is attributed to the notch blunting owing to easy splitting (delamination) crosswise to the principle crack propagation. The relationships between the crack propagation mode, the delamination fracture, and the load-displacement curve are presented and discussed. Further perspectives of tempforming applications and promising research directions are outlined.

The microstructure evolution during the annealing treatment of a recycled copper after cold rolling to total strain of 2.6 was investigated. The cold deformation resulted in the elongation of initial grains along rolling direction and the strain-induced formation of subboundaries. Annealing recovery occurred in the temperature range 100-250 °C. The recrystallized microstructures were observed after annealing at 300-400 °C. The hardness of partially recrystallized copper samples was interpreted in terms of dislocation strengthening. The recrystallization kinetics was estimated according to a Johnson–Mehl–Avrami–Kolmogorov equation using different methods for recrystallized fraction determination, i.e., the fractional softening, the grain orientation spread, and the Kernel average misorientation.

The effects of temperature and degree of tempforming deformation on the microstructure and impact toughness of high-strength low-alloy 25KhGMT steel have been considered. Tempforming forms a lamellar microstructure composed of grains and subgrains that are strongly elongated along the rolling direction. The average size of the grain section is 570–790 nm. Deformation texture includes 〈001〉 || ND and 〈111〉 || ND fibers. Tempforming increases the fracture work of this steel at lower test temperatures (KV_–40°С ≥ 360 J) due to the delamination of the specimen perpendicular to the impact direction, which prevents crack propagation towards the direction of the impact.